Abstract:A mixture of the mechanically alloyed 2Si-B-3C-N powder and short carbon fiber was hot pressed at 1800 degrees C for 30 mins in nitrogen. Careful investigation to the prepared C-fiber/2Si-B-3C-N ceramic matrix composite revealed that the composite was very difficult to be densified. Heterogeneous nucleation, abnormal grain growth and severe interface reaction occurred on the fiber surface or between the fiber and the ceramic matrix, leading to a small density and weak mechanical properties of the composite. For the prepared composite without any additive, the relative density, flexural strength, elastic modulus and fracture toughness is 71.7%, 64.6 MPa, 14.7 GPa and 1.47 MPa.m(1/2), respectively. The average size of the SiC grains close to and far away from the carbon fiber is 249.10 nm and 50.45 nm, respectively. However, with the addition of ZrO2 (7.5 mol%), the above mentioned phenomenons are changed noticeably, and those properties are significantly increased to 88.5%, 112.4 MPa, 111.1 GPa and 2.94 MPa.m(1/2), respectively. At the same time, the SiC grains close to or far away from the carbon fiber almost have the same average size of about 448.21 nm, and almost no interface reaction occurs. It shows that the addition of ZrO2 not only facilitates the sintering and densification process, but also depresses the interface reaction, promotes the homogeneous nucleation and grain growth, and hence significantly improves the mechanical properties of the C-fiber/2Si-B-3C-N composite. This interesting finding is favorable for the preparation of carbon fiber reinforced ceramic matrix composite, which requires both a large relative density and well controlled interface reaction.

Technologies and properties investigations of CNTs reinforced 3Y-ZrO2 ceramics with hot-pressing sintering

The effects of multiwalled carbon nanotubes on the hot-pressed 3 mol% yttria stabilized zirconia ceramics

Preparation and Electrical Characterization of Carbon Nanotube /zro2composite Ceramics

Zirconia-based Nanocomposite Toughened by Functionalized Multi-Wall Carbon Nanotubes

Mechanical and Electrical Properties of Chemically Modified MWCNTs/3Y-TZP Composites

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

ZrB2-CNTs Nanocomposites Fabricated by Spark Plasma Sintering

Preparation, Properties and Toughing Mechanisms of Carbon Nanotubes Reinforced Ceramic Matrix Composites

Research on the Interfacial Structure and Property Improvement of the Cfiber/2Si-B-3C-N Ceramic Matrix Composite

Effect of carbon nanotubes on the properties of ZrB2–SiC ceramics

Study on Zrc-20vol.%Sicw Ultrahigh Temperature Ceramics by Hot Pressing

Microstructures and Mechanical Properties of Cf/ZrB2-SiC Composite Fabricated by Nano Slurry Brushing Combined with Low-Temperature Hot Pressing

Study on toughening effect of zirconia nanocomposites

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Microstructure and Mechanical Properties of Piezoelectric Materials Toughening Multi-walled Carbon Nanotubes/Hydroxyapatite Biocomposites

Mechanical properties and toughening mechanisms of SiCw/ZrO2 (6% mol Y2O3) ceramic composites

Fabrication and properties of CNTS/AlN ceramics

Enhanced Toughness of KZr2(PO4)3 Ceramics Via Hydrothermal Incorporation of Multi-Walled Carbon Nanotubes

Characterization and mechanical properties of Cf/ZrB2-SiC composites fabricated by a hybrid technique based on slurry impregnation, polymer infiltration and pyrolysis and low-temperature hot pressing

Novel TiC-based composites with enhanced mechanical properties