Preparation of unidirectional porous yttria stabilized zirconia ceramics by an alginate self assemble method

Yue Zhang,Bozhi Hou,Xiuhui Wang,Jinlong Yang,Ning Ma,Yali Wang,Yong Huang

DOI: https://doi.org/10.14062/j.issn.0454-5648.2016.06.01

2016-01-01

Abstract:Porous yttria-stabilized zirconia (YSZ) ceramics with honeycomb-like pore structures were prepared by an alginate self-assembly gelation method. The unidirectional and gradual diffusion of Ca ions into the alginate sol that contains YSZ particles result in the formation of highly ordered channels arranged parallel to the direction of diffusion. The obtained porous YSZ ceramics possess a uniform pore distribution and a high cell density of 25 000 cpsi (cells per square inch). The average pore size, channel wall thickness and porosity of the sample are 140 μm, 25 μm and 74.9%, respectively. The microstructure and properties of porous YSZ ceramics are greatly affected by the initial solid loading of the slurries. When the solid loading is increased from 5% to 15%, the channel wall thickness and mechanical strength of the samples are greatly increased. Additionally, it is indicated that when the solid loading is further increased to 20%, the sample forms a special porous microstructure with a high total porosity of 79.6%.