Abstract:It is well known that aqueous gel-casting is challenging to prepare high-porosity ceramics due to the considerable drying shrinkage, cracking, and deformation of green bodies during drying caused by the high surface tension of water. Porous Y 2 SiO 5 ceramics with high porosity were prepared by introducing carbon fibers as a support material in the drying process of aqueous gel-casting to reduce shrinkage during drying. Burning out the carbon fibers after drying does not negatively affect the properties of the porous ceramic. As prepared green bodies by aqueous gel-casting have low shrinkages of 8.69%–6.81% during drying processes and high compressive strength of 13.73 ± 1.55–10.66∼0.49 MPa. The higher compressive strength of the green body has a positive significance for processing porous ceramics into special-shaped structures. As prepared porous Y 2 SiO 5 ceramics have high porosity of 73.94%–87.71%, lightweights of 1.16–0.55 g•cm 3 , extremely low thermal conductivities of 0.134 ± 0.006 to 0.051 ± 0.001 W•m −1 •k −1 , relatively low dielectric constants of 2.34–1.58, and tan δ are lower than 1.25 × 10 −3 . Porous Y 2 SiO 5 ceramics with excellent dielectric properties and thermal insulation properties meet the requirements of thermal insulation and wave transmission integration of radome materials. Aqueous gel-casting also enriches the preparation methods of high-porosity Y 2 SiO 5 ceramics.

Porous YSZ Ceramics by Water-Based Gelcasting

High-strength porous YSZ ceramics fabricated by TBA-based gelcasting with high solid loading slurry

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Porous α-Al2O3 ceramics prepared by gelcasting

Porous yttria-stabilized zirconia ceramics with low thermal conductivity via a novel foam-gelcasting method

Preparation of porous ceramics by gelcasting approach

A Novel Way to Fabricate Highly Porous Fibrous YSZ Ceramics with Improved Thermal and Mechanical Properties

Microstructure and permeability of porous YSZ ceramics with aligned and gradient pore channels fabricated by freeze casting

Influence of Solid Loading in the Gel-Casting Process on the Microstructure and Properties of Porous YSZ Ceramics

Porous Ysz Ceramics Reinforced By Different Kinds Of Fibers

Effects of Pore-Forming Agent Content on the Properties of Porous 8ysz Ceramics by Tba Based Gel-Casting

Fabrication and Properties of Highly Porous Ceramics via Gel Casting Using Steel Slag as a Novel Gelation Agent

Porous mullite ceramics from national clay produced by gelcasting

Preparation of unidirectional porous yttria stabilized zirconia ceramics by an alginate self assemble method

Near Net Shape Fabrication of Porous Cordierite by Combination of Foam Gel‐casting and Freeze‐drying

Recent Developments in Gelcasting of Ceramics

Water based gelcasting of lead zirconate titanate

Ceramics with Ultra‐Low Density Fabricated by Gelcasting: an Unconventional View

Microstructure and properties of highly porous Y2SiO5 ceramics produced by a new water-based freeze casting

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

Preparation of porous Y 2 SiO 5 ceramics with high porosity and extremely low thermal conductivity for radome applications