Preparation of porous Y 2 SiO 5 ceramics with high porosity and extremely low thermal conductivity for radome applications

Yuhan Ren,Biao Zhang,Jian Ye,Qiang Liu,Ye Gao,Haoqian Zhang,Zhaoxin Zhong,Yang Wang,Feng Ye

DOI: https://doi.org/10.1016/j.ceramint.2022.09.212

IF: 5.532

2022-12-10

Ceramics International

Abstract:It is well known that aqueous gel-casting is challenging to prepare high-porosity ceramics due to the considerable drying shrinkage, cracking, and deformation of green bodies during drying caused by the high surface tension of water. Porous Y 2 SiO 5 ceramics with high porosity were prepared by introducing carbon fibers as a support material in the drying process of aqueous gel-casting to reduce shrinkage during drying. Burning out the carbon fibers after drying does not negatively affect the properties of the porous ceramic. As prepared green bodies by aqueous gel-casting have low shrinkages of 8.69%–6.81% during drying processes and high compressive strength of 13.73 ± 1.55–10.66∼0.49 MPa. The higher compressive strength of the green body has a positive significance for processing porous ceramics into special-shaped structures. As prepared porous Y 2 SiO 5 ceramics have high porosity of 73.94%–87.71%, lightweights of 1.16–0.55 g•cm 3 , extremely low thermal conductivities of 0.134 ± 0.006 to 0.051 ± 0.001 W•m −1 •k −1 , relatively low dielectric constants of 2.34–1.58, and tan δ are lower than 1.25 × 10 −3 . Porous Y 2 SiO 5 ceramics with excellent dielectric properties and thermal insulation properties meet the requirements of thermal insulation and wave transmission integration of radome materials. Aqueous gel-casting also enriches the preparation methods of high-porosity Y 2 SiO 5 ceramics.

materials science, ceramics