Abstract:The design of super thermal insulation and high-temperature resistant materials for high temperature furnaces is crucial due to the energy crisis and the huge wasting. Although it is told that numerous studies have been reported about various of thermal insulation materials prepared by different methods, the applications of yttria-stabilized zirconia (YSZ) ceramic foams fabricated through tert-butyl alcohol (TBA)-based gel-casting process in bulk thermal isolators were barely to seen. In this paper, highly porous yttria-stabilized zirconia (YSZ) ceramic foams were fabricated by a novel gel-casting method using tert-butyl alcohol (TBA) as solvent and pore-forming agent. Different raw material ratio, sintering temperature and soaking time were all investigated to achieve optimal thermal insulation and mechanical properties. We can conclude that porosity drops gradually while compressive strength increases significantly with the rising temperature from 1000-1500°C. With prolonged soaking time, there is no obvious change in porosity but compressive strength increases gradually. All specimens have uniformly distributed pores with average size of 0.5-2μm and show good structural stability at high temperature. The final obtained ceramic foams displayed an outstanding ultra-low thermal conductivity property with only 200.6 °C in cold surface while the hot side was 1000 °C (hold 60 min to keep thermal balance before testing) at the thickness of 10 mm.

A Novel Way to Fabricate Highly Porous Fibrous YSZ Ceramics with Improved Thermal and Mechanical Properties

YSZ fiber-reinforced porous YSZ ceramics with lowered thermal conductivity: Influence of the sintering temperature

Fabrication and Properties of Porous Yttria-Stabilized Zirconia Ceramics

High-strength porous YSZ ceramics fabricated by TBA-based gelcasting with high solid loading slurry

Porous yttria-stabilized zirconia ceramics with ultra-low thermal conductivity

Effect of YSZ fiber addition on microstructure and properties of porous YSZ ceramics

Porous yttria-stabilized zirconia ceramics with low thermal conductivity via a novel foam-gelcasting method

Correction To: Porous Yttria-Stabilized Zirconia Ceramics with Low Thermal Conductivity Via a Novel Foam-Gelcasting Method

Influence of Solid Loading in the Gel-Casting Process on the Microstructure and Properties of Porous YSZ Ceramics

Effect of Sintering Temperature on Compressive Strength of Porous Yttria-Stabilized Zirconia Ceramics

A novel highly porous ceramic foam with efficient thermal insulation and high temperature resistance properties fabricated by gel-casting process

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Al 2 O 3 -fiber-reinforced porous YSZ ceramics with high mechanical strength

Novel YSV Fiber Strengthened (la <sub>0.2</sub>nd <sub>0.2</sub>sm <sub>0.2</sub>gd <sub>0.2</sub>yb <sub>0.2</sub>) <sub>2</sub>zr <sub>2</sub>o <sub>7</sub> Porous Ceramics Toward Ultralow Thermal Conductivity and Enhanced Mechanical Property

Porous Ysz Ceramics Reinforced By Different Kinds Of Fibers

Improved heat insulation and mechanical properties of highly porous YSZ ceramics after silica aerogels impregnation

Microstructure and permeability of porous YSZ ceramics with aligned and gradient pore channels fabricated by freeze casting

Microstructure and properties of highly porous Y2SiO5 ceramics produced by a new water-based freeze casting

Control of pore channel size during freeze casting of porous YSZ ceramics with unidirectionally aligned channels using different freezing temperatures

Preparation and Characterization of YSZ Porous Ceramic Tubes with a High Porosity by Wet Method

Porous Ysz Ceramics with Unidirectionally Aligned Pore Channel Structure: Lowering Thermal Conductivity by Silica Aerogels Impregnation