Preparation of hollow fiber membranes from mullite particles with aid of sintering additives
Hua Liu,Jinyun Liu,Zhou Hong,Shengxian Wang,Xuechao Gao,Xuehong Gu
DOI: https://doi.org/10.1007/s40145-020-0420-7
IF: 11.534
2020-10-21
Journal of Advanced Ceramics
Abstract:Abstract Porous mullite hollow fiber membranes were prepared with a combined phase-inversion and sintering method, using three sintering additives including yttrium stabilized zirconia (YSZ), small mullite particles (SMP), and titanium oxide (TiO 2 ) to promote the particle sintering. The results indicated that all the three additives could improve the sintering performance of mullite hollow fiber membranes due to the decrease in activation energy of mullite grains. Both YSZ and TiO 2 could react with mullite grains to generate composite oxides (e.g., ZrSiO 4 and Al 2 TiO 5 ) during sintering, following a reaction-sintering mechanism. Interestingly, the newly generated ZrSiO 4 was instable and further decomposed into monoclinic ZrO2 and SiO2 in the sintering process. The decomposition could avoid excessive embedment of composite oxides among mullite grains which have negative impact on mechanical strength of mullite hollow fibers. Overall, the doping of YSZ provided a better promotion effect on the sintering of mullite hollow fiber membranes, where the microstructural and mechanical properties are insensitive to the doping content and sintering temperatures, so it could be used as the candidate for the large-scale preparation of mullite hollow fibers.
materials science, ceramics