Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure and Corrosion Behavior of As-Homogenized Mg-xLi-3Al-2Zn-0.2Zr Alloys (x=5, 8, 11 Wt%)

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Improving the corrosion resistance of Mg-8Li-3Al-2Zn alloy by combining Gd alloying and hot extrusion

Role of alloyed Al on the microstructure and corrosion behavior of as-cast dilute Mg-2Zn- x Al-0.5Ca alloys

Microstructure, Mechanical Properties, and Corrosion Behavior of Al-4.0Cu-1.1Li-0.5Mg-xAg Alloys

Microstructure, Mechanical Properties and Corrosion Behavior of Mg-Zn-Zr Alloys with Different Compositions

Microstructure and Corrosion Behavior of the As-cast Mg-xAl (x=9%, 12%, 15%) Alloys

Effect of Al on Microstructure and Mechanical Properties of Mg-10Li-3Zn-1Y Alloys

Precipitate microstructures, mechanical properties and corrosion resistance of Al-1.0 wt%Cu-2.5 wt%Li alloys with different micro-alloyed elements addition

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructure, Mechanical Properties and Corrosion Behaviors of Al–Li–Cu–Mg–Ag–Zn Alloys

Investigation on the microstructural evolution and corrosion behaviors of Zn-microalloyed Al-Cu-Li alloys

Corrosion behavior characterization of as extruded Mg-8Li-3Al alloy with minor alloying elements (Gd, Sn and Cu) by scanning Kelvin probe force microscopy

Effect of Zn Content and Homogenization Treatment on Mechanical Properties and Corrosion Behavior of Mg-9Y-xZn Alloys

Microstructure and corrosion resistance of ultrahigh pressure Mg-8Li based alloys

Microstructure, mechanical properties and corrosion behavior of extruded Mg-Zn-Ca alloys with same Zn/Ca atomic ratio

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Study on the Microstructure and Corrosion Behavior of Mg–(4 − X)gd–xy–2zn (x = 0, 2, 4 Wt%) Alloy

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates

Microstructure characterization and corrosion behavior of Mg–Y–Zn alloys with different long period stacking ordered structures