Microstructure and Corrosion Behavior of the As-cast Mg-xAl (x=9%, 12%, 15%) Alloys

Guo Yanping,Wang Yaning,Wang Quanle,Dong Zhaobo,Wang Lin,Fang Daqing,Liu Baosheng

2018-01-01

Rare Metal Materials and Engineering

Abstract:Mg-xAl (x=9%, 12%, 15%, mass fraction) alloys were prepared by semi-continuous casting. The effects of Al contents on microstructure evolution of Mg-Al alloy were investigated using X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM). Meanwhile, the corrosion behaviors of the Mg-xAl alloys were studied by both hydrogen evolution and potentiodynamic polarization curves. Moreover, the corrosion mechanism of Mg-xAl alloys was also discussed based on the SEM corrosion morphologies of as-cast Mg-Al alloys after hydrogen evolution testing for 72 h in 3.5% NaCl without corrosion products. The results indicate that the microstructure of the three alloys is composed of alpha-Mg phase and beta-Mg17Al12 phase. Moreover, the content of beta phase increases with the increase of Al content. As a result, the corrosion resistance of the three alloys is enhanced with the increase of the beta phase. The Mg-15%Al alloy has the best corrosion resistance, while Mg-9%Al has the worst. The oxide film forms on the surface of all the as-cast Mg-Al alloys after hydrogen evolution testing for 72 h in 3.5% NaCl. Furthermore, the stability of the film increases with the increase of Al content.