Abstract:A comprehensive research project consisting of pilot-scale combustion testing and long-term laboratory corrosion study has been performed. A pilot-scale combustion facility was modified to enable burning of pulverized coals under the conditions typical for coal-fired utility boilers. Eight United States (U.S.) coals were selected for this investigation, with the test conditions for all coals set to have the same heat input to the combustor. In addition, the air/fuel ratio was controlled so that approximately 3% excess oxygen was attained in the combustion gas at the furnace outlet, a location equivalent to the furnace exit of commercial boilers. During each pilot-scale combustion test, extensive online measurements of the flue gas compositions were performed. In addition, deposit samples were collected at the same location for chemical analyses. This information characterized well the combustion environments adjacent to the superheaters and reheaters of utility boilers burning different U.S. coals. The gas and deposit compositions were then simulated in a series of 1000-hour laboratory corrosion tests in which the corrosion performances of different alloys were evaluated at 704oC (1300oF). Results of this laboratory study led to better understanding of the corrosion mechanisms operating on superheaters and reheaters in coal-fired boilers due to the mutual presence of sulfur and chlorine in coal. A new corrosion mechanism, i.e., “Active Sulfide-to-Oxide Corrosion Mechanism,” accounts for the rapid corrosion attack on low-alloy ferritic steels and lower-grade stainless steels resulting from the formation of iron chloride (FeCl2) vapor and associated cycling reactions. For higher alloys containing sufficient chromium, the attack is dominated by Hot Corrosion in the presence of a fused salt. In addition, two stages of the hot corrosion mechanism have been elucidated here in detail. The initiation of hot corrosion attack induced by molten sulfate may involve Stage 1 “acidic” fluxing and re-precipitation of the protective scale formed initially on the deposit-covered alloy surfaces, followed by Stage 2 Hot Corrosion dominated by “basic” fluxing and re-precipitation after the scale is locally penetrated by the fused salt.

Effect of Alloying Chemistry on Fireside Corrosion Behavior of Ni–Fe-Based Superalloy for Ultra-supercritical Boiler Applications

Effect of Cobalt Content on the Oxidation and Corrosion Behavior of Ni–Fe-Based Superalloy for Ultra-Supercritical Boiler Applications

Effect of Alloying Additions on Oxidation Behaviors of Ni‐Fe Based Superalloy for Ultra‐Supercritical Boiler Applications

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Investigation of the Fireside Corrosion of a New Wrought Ni-Fe-Cr-based Alloy in Advanced Ultra-Supercritical Steam Boilers

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Effect of Heat Treatment on Corrosion Behavior of a Newly Developed N-i Fe Based Superalloy in Simulated Coal Ash/Gas Environment

High-temperature corrosion behaviours of nickel–iron-based alloys with different molybdenum and tungsten contents in a coal ash/flue gas environment

Effects of Different Surface Native Pre-Oxides on the Hot Corrosion Properties of Nickel-Based Single Crystal Superalloys

Investigation of Fireside Corrosion of Austenitic Heat-Resistant Steel 10cr18ni9cu3nbn in Ultra-Supercritical Power Plants

Effect of High Flow Velocity on Corrosion Behavior of Ni Based and Ni-Fe Based Alloys in Supercritical Water Oxidation Environment

Fireside Corrosion Behaviors Of Super304h And Hr3c In Coal Ash/Gas Environment With Different So2 Contents At 650 Degrees C

Fireside Corrosion Behaviors of Super304H and HR3C in Coal Ash/Gas Environment with Different SO 2 Contents at 650 °C

High-Temperature Corrosion Mechanisms for Selected Iron and Nickel-Based Alloys Exposed to Sulfur and Chlorine-Containing Environments

A Study of the Hot Salt Corrosion Behavior of Three Nickel-Based Single-Crystal Superalloys at 900 °C

Effect of Al content on steam oxidation behavior for ferritic Fe-21Cr-xAl alloys

Effects of Long Term Thermal Exposure on Microstructure and Mechanical Property Evolution of a New Wrought Ni–Fe Based Superalloy

Effect of oxygen concentrations on the corrosion behavior of a duplex-phase FeNiCrCuAl high entropy alloy in supercritical water

Effects of Ni and Cr on the high-temperature oxidation behavior and mechanisms of Co- and CoNi-base superalloys

High-temperature oxidation and hot corrosion of Ni-based single crystal superalloy in the incubation stage

Insights into Oxidation and Nitridation of Alumina-Forming FeCrAl Alloy after Supercritical Water Exposure: Effect of Pre-Corrosion on High-Temperature Damage Behavior