Abstract:A comprehensive research project consisting of pilot-scale combustion testing and long-term laboratory corrosion study has been performed. A pilot-scale combustion facility was modified to enable burning of pulverized coals under the conditions typical for coal-fired utility boilers. Eight United States (U.S.) coals were selected for this investigation, with the test conditions for all coals set to have the same heat input to the combustor. In addition, the air/fuel ratio was controlled so that approximately 3% excess oxygen was attained in the combustion gas at the furnace outlet, a location equivalent to the furnace exit of commercial boilers. During each pilot-scale combustion test, extensive online measurements of the flue gas compositions were performed. In addition, deposit samples were collected at the same location for chemical analyses. This information characterized well the combustion environments adjacent to the superheaters and reheaters of utility boilers burning different U.S. coals. The gas and deposit compositions were then simulated in a series of 1000-hour laboratory corrosion tests in which the corrosion performances of different alloys were evaluated at 704oC (1300oF). Results of this laboratory study led to better understanding of the corrosion mechanisms operating on superheaters and reheaters in coal-fired boilers due to the mutual presence of sulfur and chlorine in coal. A new corrosion mechanism, i.e., “Active Sulfide-to-Oxide Corrosion Mechanism,” accounts for the rapid corrosion attack on low-alloy ferritic steels and lower-grade stainless steels resulting from the formation of iron chloride (FeCl2) vapor and associated cycling reactions. For higher alloys containing sufficient chromium, the attack is dominated by Hot Corrosion in the presence of a fused salt. In addition, two stages of the hot corrosion mechanism have been elucidated here in detail. The initiation of hot corrosion attack induced by molten sulfate may involve Stage 1 “acidic” fluxing and re-precipitation of the protective scale formed initially on the deposit-covered alloy surfaces, followed by Stage 2 Hot Corrosion dominated by “basic” fluxing and re-precipitation after the scale is locally penetrated by the fused salt.

Investigation of the Fireside Corrosion of a New Wrought Ni-Fe-Cr-based Alloy in Advanced Ultra-Supercritical Steam Boilers

Effect of Alloying Chemistry on Fireside Corrosion Behavior of Ni–Fe-Based Superalloy for Ultra-supercritical Boiler Applications

Fireside Corrosion Behaviors of Super304H and HR3C in Coal Ash/Gas Environment with Different SO 2 Contents at 650 °C

Fireside Corrosion Behaviors Of Super304h And Hr3c In Coal Ash/Gas Environment With Different So2 Contents At 650 Degrees C

Effect of Heat Treatment on Corrosion Behavior of a Newly Developed N-i Fe Based Superalloy in Simulated Coal Ash/Gas Environment

High-temperature corrosion behaviours of nickel–iron-based alloys with different molybdenum and tungsten contents in a coal ash/flue gas environment

Effect of Alloying Additions on Oxidation Behaviors of Ni‐Fe Based Superalloy for Ultra‐Supercritical Boiler Applications

Effect of Cobalt Content on the Oxidation and Corrosion Behavior of Ni–Fe-Based Superalloy for Ultra-Supercritical Boiler Applications

High‐temperature corrosion behaviors of typical nickel alloy coatings in a simulated boiler coal ash/gas environment in the Zhundong region

Investigation of Precipitation Behavior of a Novel Ni-Fe-Based Superalloy during High-Temperature Aging Treatment

Corrosion Behavior of Nb-doped FeCrAl Alloy in 500°C Steam

Research Progress of HR3C Heat Resistant Steel Used in Ultra Supercritical Boiler

A New Wrought Ni–Fe-base Superalloy for Advanced Ultra-Supercritical Power Plant Applications Beyond 700 °C

Comparison and mechanism research of corrosion behavior of materials used in supercritical water-cooled reactors

High-Temperature Corrosion Mechanisms for Selected Iron and Nickel-Based Alloys Exposed to Sulfur and Chlorine-Containing Environments

Effect of Cr and Y on the microstructure and mechanical properties of Fe-Cr-Al alloys during corrosion-aging in superheated steam at 500 °C

High-temperature corrosion data and mechanisms for T122, Super304H and HR3C after 15 years in 1000MW ultra-supercritical power plant

Creep rupture of a Ni-Fe based model alloy under simulated fireside corrosion in coal-fired boilers

Corrosion of New Zirconium Claddings in 500 °C/10.3 MPa Steam: Effects of Alloying and Metallography

Comparative investigation on thermal corrosion of alloy coatings in simulated waste incinerator environment

Addressing challenges in high-temperature oxidation of ultra-supercritical boiler tubes via FeCoNiCrMo high-entropy alloy coatings