High temperature oxidation behavior and mechanism of a new Ni-Co-based superalloy
Xinpeng Zhuang,Yi Tan,Xiaogang You,Pengting Li,Longhai Zhao,Chuanyong Cui,Huixing Zhang,Hongyang Cui
DOI: https://doi.org/10.1016/j.vacuum.2021.110219
IF: 4
2021-07-01
Vacuum
Abstract:<p>The oxidation behavior and mechanism of a new Ni-Co-based superalloy developed for advanced engine turbine disks, were investigated at various temperature for different exposure times. The isothermal oxidation experiments, scanning electron microscope (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD) and electron probe microanalysis (EPMA) were employed to analyze the oxidation characteristics of the new Ni-Co-based superalloy. The results show that the oxidation kinetics can be described by a parabolic law at each temperature and the oxidation rate constants K at temperature of 800 °C, 900 °C and 1000 °C are 0.015, 0.033 and 0.138 mg<sup>2</sup> cm<sup>−4</sup> h<sup>−1</sup>, respectively. The oxidation process is controlled by out-diffusion of metallic elements and in-diffusion of oxygen. Multifarious oxides are formed on the surface of the alloy due to the complex alloying elements. The oxide scale is consisted of three parts: the external oxide layer containing TiO<sub>2</sub> and a small amount of Cr<sub>2</sub>O<sub>3</sub>; the middle oxide layer consisted of Cr<sub>2</sub>O<sub>3</sub>, TiO<sub>2</sub>, Al<sub>2</sub>O<sub>3</sub> and the spinel phase; the internal oxide layer comprised of Al<sub>2</sub>O<sub>3</sub>. With further oxidation, TiO<sub>2</sub> accumulates gradually on the external oxide layer because of the large diffusion distance of Ti, while O penetrated into the matrix can be captured by Al to prevent the further diffusion into alloy interior.</p>
materials science, multidisciplinary,physics, applied