Effect of Cr content on the high temperature oxidation behavior of FeCoNiMnCr x porous high-entropy alloys
Ying Wang,Dong Li,Shengding Wang,Mao Zhang,Pan Gong,Zhigang Hu,Bin Li
DOI: https://doi.org/10.1016/j.jmrt.2024.10.025
IF: 6.267
2024-10-10
Journal of Materials Research and Technology
Abstract:FeCoNiMnCr porous high-entropy alloys were prepared using the activation reaction sintering method with Fe, Co, Ni, Mn, and Cr as raw materials. The oxidation behaviors of FeCoNiMnCr x porous high-entropy alloys with different Cr contents, such as pore structure, the surface oxide film phase composition, structure, and morphology, were characterized by X-ray diffraction (XRD), electron probe micro analysis (EPMA), energy dispersive X-ray spectroscopy (EDS), and pore tester after high-temperature oxidation at 800–1000 °C. The results indicate that the initial porous high-entropy alloy comprises a single FCC solid solution phase. With the increase in Cr content, the average pore diameter, average porosity, and air permeability of the porous high-entropy alloy also increase. The oxidation kinetics of the porous high-entropy alloy after exposure to temperatures between 800 °C and 1000 °C follows a single-stage parabolic evolution law. At the same oxidation temperature, With the increase of Cr content, the oxidation gains gradually increased, at the same Cr content at different temperatures, the antioxidant performance of 1000 °C was the weakest, followed by 800 °C, and 900 °C showed excellent antioxidant performance. The oxidation products are mainly Mn 2 O 3 , Mn 3 O 4 , (Mn, Cr) 3 O 4 , Cr 2 O 3 and Fe 2 O 3 .
materials science, multidisciplinary,metallurgy & metallurgical engineering