Abstract:We present a comparative study on oxidation behavior and failure mechanisms of conventional NiCoCrAl alloys doped with Y and Hf (CNA) and in-situ composite AlCoCrFeNi 2.1 eutectic high-entropy alloy doped with Y and Hf (ISC-EHEA) at 1300 °C. We demonstrate that the ISC-EHEA has much stronger resistance to surface rumpling and oxide spallation than CNA. Hybrid molecular dynamics (MD) and Monte Carlo (MC) simulations show that the diffusion coefficients of the metal elements in the Al-depletion layer of the ISC-EHEA are 50 % lower than those in the CNA. The low diffusion coefficients lead to low growth stress in the thermally grown Al 2 O 3 scale on the ISC-EHEA and improve the creep resistance of the metal in contact with the scale, thus preventing the occurrence of rumpling. The oxidation rate constant of the ISC-EHEA is ∼32 % lower in comparison to those of the CNA, which is attributed to the coarser columnar Al 2 O 3 grains that effectively mitigate grain boundary diffusion. The rumpling-free metal/oxide interface, the low residual stress and the low oxide growth rate for the ISC-EHEA result in strong resistance to scale spallation. Owing to the strong scale/alloy bonding at the interface and the build-up of strain energy during prolonged oxidation, damage in the Al 2 O 3 scale on the ISC-EHEA is initiated as surface cracks rather than interface decohesion. When re-oxidized at 1300 °C, the ingress of oxygen along the surface cracks results in fast growth of new oxides at the metal/oxide interface, which causes local stress concentration, interface crack propagation and scale spallation.

Unraveling the oxidation mechanism of an AlCoCrFeNi high-entropy alloy at 1100 °C

Unraveling the oxidation mechanism of Y-doped AlCoCrFeNi high-entropy alloy at 1100 °C

A comparative study on the oxidation behavior and failure mechanisms of conventional NiCoCrAl alloy and in-situ composite AlCoCrFeNi 2.1 eutectic high-entropy alloy at 1300 °C

High-temperature oxidation behaviors of an equiatomic CrMnFeCoNi high entropy alloy

Effect of Al content on the oxidation behavior of Y/Hf-doped AlCoCrFeNi high-entropy alloy

High temperature oxidation behavior and mechanism of Al0.3CuCrFeNi2 high-entropy alloy with a coherent γ/γ' microstructure

Oxidation behavior of gas-atomized AlCoCrFeNi high-entropy alloy powder at 900-1100 °C

High-Temperature Oxidation Behavior of Al-Co-Cr-Ni-(Fe or Si) Multicomponent High-Entropy Alloys

Microstructure and oxidation behavior of the Y/Ta/Hf co-doped AlCoCrFeNi high-entropy alloys in air at 1100 °C

High Temperature Oxidation Behavior of Al0.5CrCoFeNi High Entropy Alloy

High oxidation resistance of AlCoCrFeNi high entropy alloy through severe shear deformation processing

Enhanced Oxidation Resistance of Ultrafine-Grain Microstructure AlCoCrFeNi High Entropy Alloy

New insights in the oxidation behavior of (FeCoCrNi)94Al4Ti2Si high entropy alloys at 1100 °C

Revealing the oxidation behavior of AlCr x FeNi lightweight multi-principal element alloys via experimental and first-principles calculations

Effect of initial grain size on oxidation resistance of L1 2 -strengthened Al-Fe-Cr-Cu-Ni high-entropy alloy at 900 °C

The oxidation behavior of the CrFeCoNiAlx (x = 0, 1.0, and 5.0 wt%) high-entropy alloy synthesized with Al elemental powder via powder bed fusion technique at high temperatures

Improving the high temperature oxidation resistance of high entropy alloy by surface modification

Microstructure and Early-Stage Oxidation Behavior of Co-Cr-Cu-Fe-Mn-Ni High-Entropy Alloys

Electronic-scale assessment of high-temperature oxidation mechanisms in a novel Fe-based alloy

Microstructure and atmospheric oxidation behavior of CrCuFeMnNiCox high‐entropy alloys fabricated by vacuum hot‐press sintering

High-Temperature Oxidation Behavior of FeCoCrNi+(Cu/Al)-Based High-Entropy Alloys in Humid Air