Abstract:In the present study, ZrB2 nanoparticles were synthesized using sol-gel method. Zirconium alkoxide was used as the source of zirconium and boric acid as the source of boron. The size of precursor nanoparticle was controlled using the pH parameter inside the sol, and the formation of primary nuclei of ZrB2 phase and their crystallized amount were investigated using the temperature parameter. To evaluate the mechanism of product formation during the sol-gel process, TEM, SEM, DTA/TG, RAMAN, XRD, FTIR, and DLS methods were used. DLS analysis showed that the size of precursor particle inside the sol at pH less than 5 was below 10 nm. Measurements of viscosity and zeta potential inside the sol showed that in the acidic range, the particle stability decreases with increasing pH. Mixing of precursor particles at molecular level inside the sol was one of the important reasons in reducing the synthesis temperature of ZrB2 particles. FTIR analysis on chemical bonds showed that Zr-O-B bond was formed inside the gel powder. DTA analysis showed that the primary nuclei of ZrB2 particles were formed at a temperature of about 1400 °C. XRD observations proved that the primary nuclei of the ZrB2 phase crystallized and grew at a temperature of about 1500 °C. Surface research revealed that the specific surface area of the synthesized ZrB2 particles is equivalent to 115 m2/g, and also the surfaces of these particles are porous, and the size of these porosities is in meso range. SEM analysis showed that the particle size of ZrB2 having homogeneous morphology is about 50 nm. TEM microstructural analysis revealed that ZrB2 particles were formed uniformly and orderly in very fine dimensions.Graphical abstract

Synthesis of ZrB$lt;inf$gt;2$lt;/inf$gt; Nanoparticles by Using Xylitol

Improvement of ZrB2 nanopowder synthesis by sol-gel method via zirconium alkoxide/boric acid precursors

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

A General Propylene Epoxide-assisted Sol-Gel Route for the Synthesis of ZrO2-SnO2 Composite Sols

Preparation of Zirconia Powders by Sol-gel Process

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Synthesis and Characterization of Zirconium Nitride Nanopowders by Internal Gelation and Carbothermic Nitridation

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Synthesis and Pyrolysis Evolution of Glucose-Derived Hydrothermal Precursor for Nanosized Zirconium Carbide

Carbothermal Reduction Synthesis Of Zirconium Diboride Powders Assisted By Microwave

The Self-Catalytic Role Of Zirconium N-Propoxide In Sol-Gel Syntheses Of Zro2/Y2o3-Ceo2 Compound Powders

From Gel to Crystal: Mechanism of HfO2 and ZrO2 Nanocrystal Synthesis in Benzyl Alcohol

Tunable Structure of Zirconia Nanoparticles by Biopolymer Gelation: Design, Synthesis and Characterization

Effect of Fructose on Preparation of Nanocrystalline Zirconium Nitride Powder by Internal Gelation Combined with Carbothermic Nitridation

Preparation and CO 2 Capture Properties of Nanocrystalline Li 2 ZrO 3 Via an Epoxide-Mediated Sol–gel Process

Synthesis of zirconium boride (ZrB2) rod crystals through salt-assisted boro/carbothermal reduction