Abstract:Considering that tungsten (W) materials served as the plasma-facing material in the fusion reactor would be exposed to edge-localized modes (ELMs)-like thermal shock loading accompanied with He-ion irradiation, the W–TiC composite produced with a wet-chemical method was conducted by the dual effects from the laser beam thermal shock first and He-ion irradiation later in this work. The microstructure changes of the W–TiC composite before and after two tests were characterized by scanning electron microscopy or transmission electron microscopy. After the laser beam thermal shock test, there was an obvious interface on the exposed surface of the W–TiC composite. Several main cracks and melting areas could be found nearby the interface and center, respectively. Furthermore, a mixture of tungsten oxide and TiC was easy to aggregate and form into circle areas surrounding the melting area. The thermal shock tested that W–TiC composite was then subjected to the He-ion irradiation. The typical features of fuzz structures could be detected on the surface of the W–TiC composite apart from the center of the melting area. Notably, several nano-sized He bubbles deeply distributed at grain boundaries in the melting area, owing to the grain boundary functioning as the free path for He diffusion.

Effect of Laser Beam Thermal Shock on the Helium Ion Irradiation Damage Behavior of W-TiC-Y2O3 Composites

Influence of helium ion irradiation damage behavior after laser thermal shock of W-2%vol Y<sub>2</sub>O<sub>3</sub> composites

Combined Effect of Laser Thermal Shock and Helium Ion Irradiation on W-Y2O3 Composites

Microstructure Evolutions of the W–TiC Composite Conducted by Dual-Effects from Thermal Shock and He-ion Irradiation

Effect of Y2O3 particles on the helium ion irradiation damage of W-2%Y2O3 composite prepared by wet chemical method

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Microstructure and Transient Laser Thermal Shock Behavior of W–TiC–Y2O3 Composites Prepared by Wet Chemical Method

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Damage evolutions of completely recrystallized W–Y2O3 composite evaluated using the dual effects of electron beam thermal shock and helium ion irradiation

Preparation of TiC-doped W-Ti Alloy and Heat Flux Performance Test under Laser Beam Facility

Effect of annealing on the microstructure behavior of D+-irradiated W-2vol.%TiC composite prepared by wet-chemical method

Investigation of W–B Behavior During Short Transient Events by Laser Irradiation

Thermal shock behavior of W–ZrC/Sc2O3 composites under two different transient events by electron and laser irradiation

Repair Behavior of He+-irradiated W–Y2O3 Composites after Different Temperature-Isochronal Annealing Experiments

Evaluating surface damage behavior of W-(Y0.9La0.1)2O3 composites during spark plasma sintering process improvement

Mechanical Properties and Microstructural Change of W–Y 2 O 3 Alloy under Helium Irradiation

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock

Influence of heavy ions pre-damage on the blistering and helium bubble in tungsten under helium ions irradiation

Thermal Shock Resistance and Ablation Behavior of Tib2-Cu-Ni Composite Via Combustion Synthesis

Thermal Shock Behavior of W-0.5 Wt% Y 2 O 3 Alloy Prepared Via a Novel Chemical Method