Abstract:Tungsten (W) can be used in plasma-facing components in a fusion reactor because of its excellent radiation resistance. Some studies have found that nanocrystalline metals with a high density of grain boundary show a higher ability to resist radiation damage compared to conventional coarse-grained materials. However, the interaction mechanism between grain boundary and defect is still unclear. In the present study, molecular dynamics simulations were carried out to explore the difference of defect evolution in single-crystal and bicrystal W, while the effects of temperature and the energy of the primary knocked atom (PKA) were taken into account. The irradiation process was simulated at the temperature range of 300 to 1500 K, and the PKA energy varied from 1 to 15 keV. The results show that the generation of defects is more sensitive to the energy of PKA than temperature; the number of defects increases at the thermal spike stage with the increase of the PKA energy, but the correlation with temperature is not strong. The presence of the grain boundary prevented the recombination of interstitial atoms and vacancies during the collision cascades, and the vacancies were more likely to form large clusters than interstitial atoms in the bicrystal models. This can be ascribed to the strong segregation tendency of the interstitial atoms to grain boundaries. The simulations provide useful information for understanding the role of grain boundaries in the evolution of irradiated structural defects.

Damage evolutions of completely recrystallized W–Y2O3 composite evaluated using the dual effects of electron beam thermal shock and helium ion irradiation

Influence of helium ion irradiation damage behavior after laser thermal shock of W-2%vol Y<sub>2</sub>O<sub>3</sub> composites

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Effect of Y2O3 particles on the helium ion irradiation damage of W-2%Y2O3 composite prepared by wet chemical method

Surface Damage Evolution During Transient Thermal Shock of W-2%vol Y2O3 Composite Material in Different Surfaces

Combined Effect of Laser Thermal Shock and Helium Ion Irradiation on W-Y2O3 Composites

Thermal Shock Resistance of Nanocrystalline and Ultrafine-Grained W-Y2O3-Ti Alloys

Surface Damage During Transient Thermal Load of 50% Thickness Reduced W-2% (vol.) Y2O3 Sheet with Different Recrystallization Volume Fraction

Repair Behavior of He+-irradiated W–Y2O3 Composites after Different Temperature-Isochronal Annealing Experiments

Effect of Laser Beam Thermal Shock on the Helium Ion Irradiation Damage Behavior of W-TiC-Y2O3 Composites

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock

Microstructural Evolution and Thermal Fatigue Damage Mechanism of Second-Phase Dispersion Strengthened Tungsten Composites under Repetitive Thermal Loads

Microstructure Evolutions of the W–TiC Composite Conducted by Dual-Effects from Thermal Shock and He-ion Irradiation

Mechanical Properties and Microstructural Change of W–Y 2 O 3 Alloy under Helium Irradiation

The superior thermal stability and irradiation resistance capacities of tungsten composites synthesized by simple second-phase particle component modulation

Thermal Shock Behavior of W-0.5 Wt% Y 2 O 3 Alloy Prepared Via a Novel Chemical Method

Evaluating surface damage behavior of W-(Y0.9La0.1)2O3 composites during spark plasma sintering process improvement

The Evolution of Structural Defects under Irradiation in W by Molecular Dynamics Simulation

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Investigation of W–B Behavior During Short Transient Events by Laser Irradiation