Abstract:The high brittle-to-ductile transition temperature (DBTT) of tungsten is a significant concern that hinders its use as a structural material. This study employs small punch testing over a broad temperature range to investigate the anisotropic mechanism of DBTT in as-hot rolled W-2%wt Y2O3 specimens. RD-TD specimen exhibits the highest EUS(0.75/J), highest ELS(0.08/J) and lowest TSP (∼336 °C) in three oriented materials. Multiple factors were conducted individually, revealing that the similar dislocation density, and fraction of LAGBs are not the primary determinant of the observed variations in DBTT performance. RD-TD specimen with strong {111}<112> γ-fiber texture exhibits the highest Fm that is nearly twice as high as that of RD-ND specimen and almost three times as high as that of TD-ND specimen. The relationship between the grain morphology, such as aspect ratio present on the DBTT as well as fracture mode of the material is apparent. RD-TD specimen boasts superior plastic properties, which displays an annular crack with the dome-like structure at the core and small incisions at the periphery. While, the plasticity of TD-ND and RD-ND specimens are deemed inadequate, as evidenced by the emergence of multiple lengthy and linear cracks in a particular orientation upon initial cracking. The utilization of numerous superimposed loads and the sandwich configuration of Y2O3 particles in tungsten matrix have been discovered to promote the occurrence of delamination in the thickness direction of the RD-TD specimens. The stratified structure, texture, screw dislocations, and grain aspect ratio have been identified as the pivotal factors influencing the anisotropy on DBTT and fracture analysis.

Surface Damage Evolution During Transient Thermal Shock of W-2%vol Y2O3 Composite Material in Different Surfaces

Surface Damage During Transient Thermal Load of 50% Thickness Reduced W-2% (vol.) Y2O3 Sheet with Different Recrystallization Volume Fraction

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock

Damage evolutions of completely recrystallized W–Y2O3 composite evaluated using the dual effects of electron beam thermal shock and helium ion irradiation

Thermal Shock Behavior of W-0.5 Wt% Y 2 O 3 Alloy Prepared Via a Novel Chemical Method

Thermal shock behavior of W–ZrC/Sc2O3 composites under two different transient events by electron and laser irradiation

Transient thermal shock behavior of W–Zr/Sc2O3 composites prepared via spark plasma sintering

Microstructure and Transient Laser Thermal Shock Behavior of W–TiC–Y2O3 Composites Prepared by Wet Chemical Method

Surface Cracking of Tungsten-Vanadium Alloys under Transient Heat Loads

Surface Damage and Structure Evolution of Recrystallized Tungsten Exposed to Elm-Like Transient Loads

Influence of helium ion irradiation damage behavior after laser thermal shock of W-2%vol Y<sub>2</sub>O<sub>3</sub> composites

Investigation of W–B Behavior During Short Transient Events by Laser Irradiation

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

Effect of Anisotropic Mechanism of W-2%wt Y2O3 Alloy on DBTT and Fracture Analysis under Small Punch Testing

Evaluating surface damage behavior of W-(Y0.9La0.1)2O3 composites during spark plasma sintering process improvement

Design and characterization of therm-al shock resistance of several typical zirconia reinforced alumina ceramic composites

Recrystallization Kinetics of 50% Hot-Rolled 2% Y2O3 Dispersed Tungsten