Abstract:In the present work, the feasibility and effectiveness of fabricating La2O3-doped W-based bulk using W-based composite powders of core-shell structure with W particle as a core and La(OH)3 as a shell, without hydrogen reduction treatment, was evaluated. La(OH)3 was first coated on the surface of pure W (uncoated) powders at a weight percentage of 3.50% to prepare composite (coated) powders using the electroless plating method. The uncoated and coated powders without being treated by hydrogen reduction were then sintered using spark plasma sintering (SPS) to fabricate bulks. The results showed that the core-shell structure with W particle as a core and La(OH)3 film as a shell was fabricated. La2O3-doped W-based bulk with about 2.93 wt.% La2O3 was obtained because of the transformation from La(OH)3 to La2O3. The La2O3 particles with larger sizes were distributed mainly at W grain boundaries and those with smaller sizes were distributed mainly inside W grains. The major densification mechanism of the sintered bulk from coated powders was the filling effect of La2O3 particles on the pores as compared with the sintered bulk from uncoated powders, which could be evaluated by using a two-ball sintering neck model. The relative content of O in the form of WO3 in the sintered bulk from coated powders was identical to that in the sintered bulk from uncoated powders. The W grain size of the sintered bulk from coated powders was smaller than that of the sintered bulk from uncoated powders. The thermal properties, mechanical properties, and irradiation properties of the sintered bulk from coated powders were all higher than those of the sintered bulk from uncoated powders. With the increase of sintering temperature, the evolution of the coated powders in the initial sintering period could be divided into six stages that were not completely independent and occurred in approximate sequence from the perspective of simplification. It was feasible and effective to fabricate La2O3-doped W-based bulk using the precursor W-based composite powders of core-shell structure with W particle as a core and La(OH)3 as a shell without being treated by hydrogen reduction.

Evaluating surface damage behavior of W-(Y0.9La0.1)2O3 composites during spark plasma sintering process improvement

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Excellent performance of W–Y2O3 composite via powder process improvement and Y2O3 refinement

Influence of helium ion irradiation damage behavior after laser thermal shock of W-2%vol Y<sub>2</sub>O<sub>3</sub> composites

Combined Effect of Laser Thermal Shock and Helium Ion Irradiation on W-Y2O3 Composites

Microstructure and Transient Laser Thermal Shock Behavior of W–TiC–Y2O3 Composites Prepared by Wet Chemical Method

Surface Cracking of Tungsten-Vanadium Alloys under Transient Heat Loads

Microstructural Effects of Y2O3 and TiC Additions in Tungsten

The superior thermal stability and irradiation resistance capacities of tungsten composites synthesized by simple second-phase particle component modulation

Preparation and laser shock resistance of W/Si composites

Effect of Y2O3 particles on the helium ion irradiation damage of W-2%Y2O3 composite prepared by wet chemical method

Recent Studies of Tungsten-Based Plasma-Facing Materials in the Linear Plasma Device STEP

Microstructure and mechanical properties of Y2O3 reinforced Ti6Al4V composites fabricated by spark plasma sintering

Transient thermal shock behavior of W–Zr/Sc2O3 composites prepared via spark plasma sintering

Microstructure and Failure Mechanism of Y2O3 Coating on the W Fiber in Wf/W Composites During Field Assisted Sintering

Microstructure and Properties of La2O3-doped Tungsten-Based Bulk Material and Its Densification Mechanism During Spark Plasma Sintering Process

The Effect of Y2O3 Particles on the Microstructure and Mechanical Properties of Tungsten Fiber-Reinforced Tungsten Composites

Surface Damage and Microstructure Evolution of Yttria Particle-Reinforced Tungsten Plate During Transient Laser Thermal Shock

Microstructure and Properties of W/Sm2O3 Composites Prepared Spark Plasma Sintering

Study on forming process and performance of nano-La 2 O 3 reinforced tungsten-based composites by selective laser melting

The microstructure and deformation behavior of W-SiC composites via spark plasma sintering