Abstract:In this paper, 0.5 wt% SiC nano particles and pure tungsten powders were thoroughly mixed using ball milling, followed by sintering the mixture using Spark Plasma Sintering (SPS) to obtain the W-0.5SiC composite material block. Then, the effect of sintering temperature on the microstructure and mechanical properties of W-0.5SiC composite was investigated. It was found that the tungsten carbide (W 2 C) and silicon oxide (SiO 2 ) phases formed at the grain boundaris during the sintering process. Besides, the grain size of the composite increased with the increasing sintering temperature. To better understanding the mechanism of the grain growth, parameter fitting was proceeded based on the well-known grain growth power law. The grain growth parameters pointed out that the grain growth of the W-0.5SiC composite during the SPS process was mainly controlled by the surface diffusion . The hardness of 1800 °C sintered W-0.5SiC composite reached 342.2 ± 4.3 HV, and the compressive strength reaches 1417 ± 137 MPa. The digital image correlation technique was used during the compressive test of 1800 °C sintered W-0.5SiC composite to investigate the deformation behavior. The result indicated that the cracks tended to form at the edge of the sample or near the surface. The extension direction was almost parallel to the loading direction and went throughout the entire sample in at most 0.2 s.

Preparation and laser shock resistance of W/Si composites

The microstructure and deformation behavior of W-SiC composites via spark plasma sintering

Evaluating surface damage behavior of W-(Y0.9La0.1)2O3 composites during spark plasma sintering process improvement

Investigation of W–B Behavior During Short Transient Events by Laser Irradiation

Transient thermal shock behavior of W–Zr/Sc2O3 composites prepared via spark plasma sintering

The effects of SiC addition on the sintering densification, phases, microstructure and mechanical properties of W

Microstructure and Transient Laser Thermal Shock Behavior of W–TiC–Y2O3 Composites Prepared by Wet Chemical Method

Microstructure and Properties of W/Sm2O3 Composites Prepared Spark Plasma Sintering

Effects of SiC Content on Wear Resistance of Al-Zn-Mg-Cu Matrix Composites Fabricated Via Laser Powder Bed Fusion

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Characteristics of tungsten coating on silicon particles prepared by sol-gel method

Thermal shock behavior of W–ZrC/Sc2O3 composites under two different transient events by electron and laser irradiation

Preparation and Properties of BNw/Si3N4 Wave-Transparent Composites by Spark Plasma Sintering

Preparation of TiC-doped W-Ti Alloy and Heat Flux Performance Test under Laser Beam Facility

Wear Performance and Corrosion Behavior of Nano-SiCp-Reinforced AlSi7Mg Composite Prepared by Selective Laser Melting

Thermal Shock Behavior of W-0.5 Wt% Y 2 O 3 Alloy Prepared Via a Novel Chemical Method

Microstructure and Mechanical Properties of SiCp/Al Composite Fabricated by Concurrent Wire-Powder Feeding Laser Deposition

Microstructure and Performances of W–TiC–Y2O3 Composites Prepared by Mechano-Chemical and Wet-Chemical Methods

Spark Plasma Sintering of W-30Si Refractory Targets: Microstructure, Densification and Mechanical Properties

Microstructure and Thermal Shock Resistance of Zr7/8Ti1/8B2-20 Vol% SiC Composites Synthesized by Mechanical Alloying and Spark Plasma Sintering