Abstract:Surface blistering and deuterium (D) retention of heavy ion pre-irradiated (1 dpa) tungsten (W) exposed to low-energy (40 eV) and high-flux (1-2 x 10(22) D/m(2)s) D plasma has been investigated with low fluence of 0.1 x 10(27) D/m(2) and a high fluence of 2.2 x 10(27) D/m(2). Surface morphology observations show that a large number of blisters are formed on the undamaged W after low-fluence exposure while the area density of the blister will have significantly increased and blister bursting will be triggered in the case of high-fluence exposure. In contrast, the heavy ion pre-irradiation noticeably reduces the area density of blisters for both low-and high-fluence exposures. The thermal desorption spectroscopy (TDS) shows that the total D retention in the pre-damaged W is greater than that of the undamaged sample, and this trend is more significant with increasing fluence/duration of D plasma exposure. The results of positron annihilation Doppler broadening spectrometry (PA-DBS) and TDS indicate that a large number of vacancy-type defects, especially those with a higher trapping energy of D, are induced by the heavy ion pre-irradiation. The increasing defects/D-trap sites may result in two outcomes, the D concentration will disperse at each blister nucleation site and D inward diffusion is enhanced and, therefore, lead to the mitigation of D-induced blistering and increase the D retention. In addition, combined with the enhanced D inward diffusion caused by increasing exposure duration, the D retention is therefore much higher in the pre-damaged W in the case of high-fluence exposure. (C) 2018 Elsevier B.V. All rights reserved.

Influence of heavy ions pre-damage on the blistering and helium bubble in tungsten under helium ions irradiation

Mechanisms of helium irradiation blistering and surface deformation in tungsten

Key mechanistic features of swelling and blistering of helium-ion-irradiated tungsten

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Effect of Heavy Ion Pre-Irradiation on Blistering and Deuterium Retention in Tungsten Exposed to High-Fluence Deuterium Plasma

Effect of helium pre-implantation on the thermal shock performance of tungsten

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Helium-induced Hardening Effect in Polycrystalline Tungsten

Effect of the Displacement Damage from Argon Ion Irradiation on the Synergistic Effect of Helium–hydrogen in Tungsten

Effect of 3 MeV Fe<SUP>11+</SUP> ions pre-damage on blistering and deuterium retention in two tungsten grades

Effect of 3 MeV Fe11+ ions pre-damage on blistering and deuterium retention in two tungsten grades

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma

Influence of Au Ions Irradiation Damage on Helium Implanted Tungsten

Modeling irradiation-induced intragranular gas bubble in tungsten under external tensile loading

Effect of crystal orientation on low flux helium and hydrogen ion irradiation in polycrystalline tungsten

Influence of helium ion irradiation damage behavior after laser thermal shock of W-2%vol Y<sub>2</sub>O<sub>3</sub> composites

Effect of helium bubbles on the irradiation hardening of GH3535 welded joints at 650°C

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

Effects of Deuterium Plasma Exposure and Helium Ions Irradiation on Nanoindentation Hardness of Tungsten

Characterization of dose dependent mechanical properties in helium implanted tungsten