He ion irradiation resistance of W-Ni-Fe alloys with variable Ni and Fe concentrations
Sheng Liu,Te Zhu,Zhen Wang,Haiyu Xue,Peng Zhang,Runsheng Yu,Qiaoli Zhang,Ping Fan,Daqing Yuan,Guizhi Zhao,Xingzhong Cao,Haibiao Wu
DOI: https://doi.org/10.1016/j.fusengdes.2024.114310
IF: 1.905
2024-03-20
Fusion Engineering and Design
Abstract:Tungsten-nickel-iron (W-Ni-Fe) alloys, commonly known as W heavy alloys (WHAs), exhibit enhanced ductility, thermal conductivity, and mechanical attributes. These properties render WHAs highly suitable as plasma-facing materials in lieu of pure W. This investigation examines the irradiation resistance of two WHAs—97W-2Ni-1Fe and 90W-7Ni-3Fe—by subjecting them to He ion irradiation at doses reaching 5 × 10 17 ions/cm 2 . The study establishes that low-dose irradiation (1 × 10 17 ions/cm 2 ) inflicted negligible surface damage on both WHA compositions. Nonetheless, increasing the radiation dose to 5 × 10 17 ions/cm 2 led to observable surface impairments, albeit at a reduced magnitude when compared to pure W. An array of analytical methods was employed to characterize irradiation-induced microstructures and void swelling, including positron annihilation spectroscopy, thermal desorption spectroscopy, and transmission electron microscopy. These analyses revealed that low-dose irradiated WHAs predominantly generated vacancy-type defects. Moreover, these defects evolved into He m V n and He m V n -NiFe complexes as the irradiation dose increased. Concurrently, He bubble density escalated with rising irradiation dosage. When subjected to an irradiation dose of 1 × 10 17 ions/cm 2 , both alloys manifested desorption levels approximately 6.5 times greater than that observed in pure W. The findings of this investigation offer valuable insights to the understanding of WHA irradiation behavior in nuclear materials.
nuclear science & technology