Abstract:In this work, a thin film transistor (TFT) with Zr-doped aluminum-zinc-tin oxide (Zr-AZTO) semiconductor as active layer was investigated. The Zr-AZTO thin films were co-sputtered by ZrO2 and AZTO targets (RF-Sputter) in Ar, and annealed at 350 degrees C in air atmosphere. With the discharge power of AZTO increasing from 100 W to 120 W, the content of Zr element decreases from 0.63 +/- 0.01 at.% to 0.34 +/- 0.01 at.%, and the oxygen vacancy decreases from (19.0 +/- 0.1)% to (17.3 +/- 0.8)%. The results of Zr-AZTO thin film show that the main factor is the co-sputter power of ZrO2 target. With the co-sputter power of ZrO2 increasing from 15 W to 45 W, the content of Zr element increases from 0.63 +/- 0.01 at.% to 2.79 +/- 0.01 at.%, the content of oxygen vacancy decreases from (19.0 +/- 0.1)% to (14.1 +/- 0.1)%, Eg increases from 2.76 eV to 2.86 eV, and the root mean square (RMS) roughness firstly decreases from 0.402 nm to 0.387 nm and then increases to 0.490 nm. The Micro Wave Photo Conductivity Decay (mu-PCD, LTA-1620SP) was used to measure the quality of Zr-AZTO thin film and the mean peak and D value decreases from 139.3 mV to 80.9 mV and from 1.54 to 0.77 as the co-sputter power of ZrO2 increases from 15 W to 45 W, which means it has highest localized states and defects in high ZrO2 co-sputter power. The devices prepared at 15 W (ZrO2)/100 W (AZTO) co-sputter show a best performance, with a mu(sat) of 8.0 +/- 0.6 cm(2)/(V.S), an Ion/loff of (2.01 +/- 0.34) x 10(6), and a SS of 0.18 +/- 0.03 V/dec. The device of Sample B has a 0.5 V negative shift under -20 V NBS and 9.6 V positive shift under 20 V PBS.

Sn-Doped Zno Thin-Film Transistors with Azo, Tzo and Al Heterojunction Source/Drain Contacts

Self-Aligned Top-Gate Amorphous Zinc-Tin Oxide Thin-Film Transistor with Source/Drain Regions Doped by Al Reaction

High Performance Ti-Doped ZnO TFTs with AZO/TZO Heterojunction S/D Contacts

Enhanced Performance of A-Igzo Thin-Film Transistors by Forming AZO/IGZO Heterojunction Source/drain Contacts

High-Performance Amorphous Zinc–Tin–Oxide Thin-Film Transistors With Low Tin Concentration

Performances Of Thin Film Transistors With Ga-Doped Zno Source And Drain Electrodes

High Performance Aluminum-Doped Zno Thin Film Transistors with High-K Gate Dielectrics Fabricated at Low Temperature

High-Performance Amorphous Zinc–Tin–Oxide Thin-Film Transistors with Low Tin Concentration

48.2: Invited Paper: High Conductivity & Transparent Aluminum‐based Multi‐layer Source/drain Electrodes for Thin Film Transistors

Atomic Layer Deposition of Al-Doped ZnO Contacts for ZnO Thin-Film Transistors

Titanium doped Zinc-oxide based Thin Film Transistors: Optimization of the source/drain materials

Fully Solution-Processed Sodium Doped Zno Thin-Film Transistors Via A Low-Temperature Aqueous Route

Performance Enhancement of Fully Transparent Tin-Doped Zinc Oxide Thin-Film Transistors Fabricated by Sputtering at Low Temperature

Chitosan-Gated Low-Voltage Transparent Indium-Free Aluminum-Doped Zinc Oxide Thin-Film Transistors

Al-Doped Zno Thin-Film Transistors on Flexible Plastic Substrate

Amorphous InGaZnO Thin Film Transistors with Different Transparent Electrodes

Effect of Al Doping on Performance of ZnO Thin Film Transistors

Fully transparent al-doped ZnO thin-film transistors on flexible plastic substrates

High-Performance Flexible Tin-Zinc-Oxide Thin-Film Transistors Fabricated on Plastic Substrates

The Performance Of Zr-Doped Al-Zn-Sn-O Thin Film Transistor Prepared By Co-Sputtering

The Investigation of Indium-Free Amorphous Zn-Al-Sn-O Thin Film Transistor Prepared by Magnetron Sputtering