Microwave dielectric properties and low temperature firing of (1 − )LiZnTiO LiTiO (0.2 ≤  ≤ 0.8) ceramics with BO–CuO addition

Ying Wu,Di Zhou,Jing Guo,Li-Xia Pang

DOI: https://doi.org/10.1007/s10854-012-0962-8

2013-01-01

Abstract:In the present work, the (1 − )LiZnTiO–LiTiO (0.2 ≤  ≤0.8) ceramics were prepared via the solid state reaction method. The 0.8LiZnTiO–0.2LiTiO ceramic sample sintered at 1,160 °C for 2 h demonstrated high microwave dielectric property with a relative permittivity of 18.0, a high quality factor (Q × f) ~ 100,000 GHz (at 7.2 GHz), and a temperature coefficient of resonant frequency about −47.8 ppm/°C. With 2.0 wt% 0.4BO–0.6CuO addition, a relative permittivity of 17.5, a Q × f value of 71,000 GHz and a temperature coefficient of resonant frequency of −44.4 ppm/C can be obtained in 0.8LiZnTiO–0.2LiTiO ceramic sintered at 925 °C for 5 h and the chemical compatibility with silver electrode indicates that the ceramics may be a suitable candidate for the low temperature co-fired ceramic technology application.