Abstract:The aim of this study is to enhance the plasticity and strength of M2 high-speed steel through electron beam melting (EBM) technology. Therefore, by controlling different melting times to change the energy input, a gradient distribution of grain size and uniform distribution of carbides can be achieved. During the deformation process, the gradient structure causes geometrically necessary dislocations (GND) to accumulate near the boundary of regions in the soft zone, resulting in compressive stress in the soft zone and tensile stress in the hard zone, ultimately achieving heterogeneity-induced (HDI) work hardening. This study is to EBM technology for the design and fabrication of three types of M2 high-speed steel samples, denoted as SS-1, SS-2, and SS-3, utilizing three distinct scanning strategies: single melting, double melting, and a combination thereof. The microstructure and phase evolution of these samples were comprehensively characterized using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron backscatter diffraction (EBSD) techniques. The findings demonstrate that when sample SS-3 was subjected to the combined scanning strategy involving both single melting and double melting approaches, its crystal structure exhibited a gradient distribution along with the presence of back stress during tensile testing. Sample SS-3 achieved an average tensile strength of 1479 MPa with an average elongation rate of 1.8%. This represents an enhancement in average tensile strength by approximately 8.6% compared to sample SS-1 (∼1362 MPa) and a significant increase in average elongation rate by around 20% compared to SS-1 (∼1.44%). The gradient grain structure materials show the microstructure transformation from fine grain to coarse-grain in the same material, thus reducing the stress concentration caused by the change of mechanical properties in each region. The SS-3 sample can maintain significant ductility while improving tensile strength. Consequently, this represents a pivotal direction for the advancement of high-performance structural materials. The conducted experimental studies have demonstrated that geometrically necessary dislocations (GNDs) and their associated strain hardening play a crucial role in enhancing the strength of grain structure materials. Additionally, these are essential to achieve an exceptional synergy between strength and toughness in these materials.

Increasing Solidification Rate of M2 High-Speed Steel Ingot by Fusible Metal Mold

Improvement of mechanical property of M2 high-speed steel with hetero-microstructure tailored via electron beam melting

Study on Evolution Behavior of Carbides in Industrial‐Grade American Iron and Steel Institute M35 High‐Speed Steel Produced by Electroslag Remelting

Homogenization Treatment and Plastic Deformation Improve the Carbide Homogeneity of M42 High-Speed Steel

Microstructural evolution and tribological properties of M2 high-speed steel fabricated under various selective electron beam melting processing parameters

Microstructure, Properties and Crack Suppression Mechanism of High-speed Steel Fabricated by Selective Laser Melting at Different Process Parameters

The Influence of Insertion Depth of Inorganic Materials on Solidification Microstructure and Segregation of 2.5-ton 42CrMo Ingot

Microstructure Evolution and Precipitation Strengthening Behaviour of Additively Manufactured High-speed Steels

A modified M2 high-speed steel enhanced by in-situ synthesized core-shell MC carbides

Microstructural changes in as-cast M2 grade high speed steel during high temperature treatment

Refinement of Eutectic Carbides in M2 High Speed Steel by Adjusting Magnetic Flux Density During Magnetic Controlled ESR Process

Evolution of primary carbides during accelerated solidification process of high-carbon martensitic stainless steels

Microstructure and mechanical properties of M2 high speed steel produced by electron beam melting

Melting and Flowing Behavior of Mold Flux in a Continuous Casting Billet Mold for Ultra-High Speed

Investigation on Heat Transfer in Molds with Different Water-Cooling Structures Under Billet High-Speed Continuous Casting

High-Temperature Annealing Significantly Enhances Intrinsic Hot Workability of the As-cast High-Nitrogen M42 High-Speed Steel

Extremely high temperature carbide precipitation induced intragranular acicular ferrite transformation of M2 steel during semi-solid cooling

Improved high‐temperature softening resistance and wear resistance of AISI M42 high‐speed steel by N‐alloying

Effect of high cooling rate on the solidification microstructure of Al-Cu/TiB 2 alloy fabricated by Freeze-Ablation casting

The Inclusion Characteristics and Mechanical Properties of M2 High-Speed Steel Treated with a Vacuum Carbon Deoxidation Process

Hardening of Selective Laser Melted M2 Steel