Abstract:The aim of this study is to enhance the plasticity and strength of M2 high-speed steel through electron beam melting (EBM) technology. Therefore, by controlling different melting times to change the energy input, a gradient distribution of grain size and uniform distribution of carbides can be achieved. During the deformation process, the gradient structure causes geometrically necessary dislocations (GND) to accumulate near the boundary of regions in the soft zone, resulting in compressive stress in the soft zone and tensile stress in the hard zone, ultimately achieving heterogeneity-induced (HDI) work hardening. This study is to EBM technology for the design and fabrication of three types of M2 high-speed steel samples, denoted as SS-1, SS-2, and SS-3, utilizing three distinct scanning strategies: single melting, double melting, and a combination thereof. The microstructure and phase evolution of these samples were comprehensively characterized using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron backscatter diffraction (EBSD) techniques. The findings demonstrate that when sample SS-3 was subjected to the combined scanning strategy involving both single melting and double melting approaches, its crystal structure exhibited a gradient distribution along with the presence of back stress during tensile testing. Sample SS-3 achieved an average tensile strength of 1479 MPa with an average elongation rate of 1.8%. This represents an enhancement in average tensile strength by approximately 8.6% compared to sample SS-1 (∼1362 MPa) and a significant increase in average elongation rate by around 20% compared to SS-1 (∼1.44%). The gradient grain structure materials show the microstructure transformation from fine grain to coarse-grain in the same material, thus reducing the stress concentration caused by the change of mechanical properties in each region. The SS-3 sample can maintain significant ductility while improving tensile strength. Consequently, this represents a pivotal direction for the advancement of high-performance structural materials. The conducted experimental studies have demonstrated that geometrically necessary dislocations (GNDs) and their associated strain hardening play a crucial role in enhancing the strength of grain structure materials. Additionally, these are essential to achieve an exceptional synergy between strength and toughness in these materials.

Improved high‐temperature softening resistance and wear resistance of AISI M42 high‐speed steel by N‐alloying

Mechanism of Laser Carbonitriding Enhancing the Wear Resistance of 45# Steel

High-Temperature Annealing Significantly Enhances Intrinsic Hot Workability of the As-cast High-Nitrogen M42 High-Speed Steel

Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel

Homogenization Treatment and Plastic Deformation Improve the Carbide Homogeneity of M42 High-Speed Steel

Enhancing Dry Sliding Wear Resistance of High-Mn Austenitic Steel by Adding N

Enhanced Strength and Toughness of High Nitrogen Stainless Bearing Steel by Controlling Interstitial Partitioning Via V-microalloying

Effect of RE-Al-N on Structures and Properties of M2 Cast High Speed Steel

Effects of Austenitizing Conditions on the Microstructure of AISI M42 High-Speed Steel

Tribological Properties Against Gear-Steel of M42 Tool Steel Surface-Modified with Hard Coatings

Study on the Influence of Silicon and Aluminum on the Microstructure and Properties of Low Cobalt M42 High-Speed Steel

Influence of Tempering Time on the Microstructure and Mechanical Properties of AISI M42 High-Speed Steel

Improvement of mechanical property of M2 high-speed steel with hetero-microstructure tailored via electron beam melting

Microstructural Evolution and Mechanical Properties of the Aluminum-Alloyed Fe-1.50 Wt%B-0.40 Wt%C High-Speed Steel

Microstructure–Wear Resistance Relationship of Nitrogen-Containing High-Speed Tool Steel, AISIM41: Non-equilibrium Solidification

Influence of Ni content on impact-abrasion wear resistance of medium-carbon low alloy cast steel

Effect of Tempering Conditions on Secondary Hardening of Carbides and Retained Austenite in Spray-Formed M42 High-Speed Steel

Surface self-nanocrystallization and -lubricating dependent wear resistance of austenitic steels at same initial hardness level

Enhanced High‐Temperature Strength of a Low‐Density Dispersion‐Strengthened Fe–Mn–Al–C Steel

Ultrastrong gradient nanostructured CSS-42L bearing steel and its enhanced wear resistance at elevated temperature

The Effect of N Content on the Microstructure and Wear Resistance of Improved High-Carbon Chromium Bearing Steel