High-Temperature Annealing Significantly Enhances Intrinsic Hot Workability of the As-cast High-Nitrogen M42 High-Speed Steel

Wei-Chao Jiao,Hua-Bing Li,Hao Feng,Hai-Jian Wang,Zhou-Hua Jiang,Wei Wu
DOI: https://doi.org/10.1007/s11661-022-06673-7
2022-04-19
Metallurgical and Materials Transactions A
Abstract:One important challenge in producing high-speed steels (HSSs) by conventional route is how to improve their hot workability. In this work, the effect of high-temperature annealing on the microstructure evolution and hot deformation behavior of the as-cast high-nitrogen M42 HSS was studied. The results indicated that the as-cast microstructure of high-nitrogen M42 HSS mainly consisted of the dendrite cells of matrix, interdendritic network of M2C eutectic carbides, primary M(C,N) carbonitrides, and intradendritic fine M2C secondary carbides. After high-temperature annealing, M2C eutectic carbides were transformed into M6C and M(C,N) products via a diffusion-driven reaction of M2C + matrix → M6C + M(C,N), and M6C carbides were the dominant products. Initially, M6C and M(C,N) nucleated at the M2C/matrix interface, and then grew inward from outside. With increasing annealing temperature and time, the average length–width ratio of interdendritic mixed carbides of M2C and M6C gradually decreased. The full decomposition and breaking of M2C eutectic carbides in the as-cast high-nitrogen M42 HSS could be achieved by annealing at 1100 °C for 8 hours. Meanwhile, high-temperature annealing led to the decreased amount of intradendritic M2C secondary carbides and the formation of M6C carbides within the intradendritic region. The high-temperature annealed steel exhibited higher flow stress than the as-cast steel at most deformation conditions, but lower deformation activation energy. The macroscopic morphologies showed that the hot workability of the high-temperature annealed steel was evidently better than that of the as-cast steel, which could be attributed to its better deformation compatibility and more sufficient dynamic recrystallization (DRX). Moreover, high-temperature annealing treatment led to a more uniform carbide distribution after hot compression. Therefore, high-temperature annealing treatment may provide an opportunity to further maintain or even improve the competitiveness of HSS produced by conventional route compared with those by powder metallurgy.
What problem does this paper attempt to address?