Abstract:Nickel-based superalloy IN713C produced through investment casting route is widely used for turbocharger turbine wheels in the automotive industry. The produced microstructure and microtexture are not homogeneous across the turbine component due to geometrical factors and localised cooling rate during the casting process, which give rise to inhomogeneous deformation during service. In the present paper, two kinds of in-house fatigue tests, Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF), were conducted at 600 °C in attempt to simulate the actual fatigue conditions experienced by turbine wheels in turbocharger. From Geometrically Necessary Dislocation (GND) distributions and strain analyses, it is concluded that microstructure heterogeneity such as carbide precipitates distribution within dendritic structure network determine the failure micromechanics during LCF tests. In the early stage of LCF loading, crack principally initiated within near surface carbides that have been oxidised during high temperature exposure. The higher GND density at the tip of carbide precipitates due to oxidation volume expansion are found to facilitate easy cracks initiation and propagation. Moreover, the cluster-like carbides network and its distribution can accelerate oxidation process and crack growth effectively. Furthermore, in the later stage of crack propagation during LCF, the weak interdendrite areas rotate to accommodate increased strain leading to faster cracks propagation and hence final catastrophic failure. Serial section technique for 3-D visualisation was employed to investigate the crystallographic grain orientation correlation with fracture mechanics during HCF loading. It appears that the microtexure and grain orientations are more critical than the alloy microstructure in an area with a relatively uniform carbides distribution and weak dendrite structure where HCF failure occurred. Based on the slip trace analysis, it was found that most faceting occurred in Goss grains (<110>//LD) and on slip system with the highest Schmid factor. It is concluded that cracks were initiated on planes with high Schmid factors and assisted by the presence of porosity.

Microstructure–Wear Resistance Relationship of Nitrogen-Containing High-Speed Tool Steel, AISIM41: Non-equilibrium Solidification

Effect of nitrided-layer microstructure control on wear behavior of AISI H13 hot work die steel

Tribological Studies of Plasma Source Ion Nitrided Low Alloy Tool Steel

Effect of ammonia addition on microstructure and wear performance of carbonitrided high carbon bearing steel AISI 52100

Evolution of Microstructure and Hardness of the Nitrided Zone during Plasma Nitriding of High-Alloy Tool Steel

Effect of N2/Ar Ratio on Wear Behavior of Multi-Element Nitride Coatings on AISI H13 Tool Steel

Nitriding Effect on the Tribological Performance of CrN-, AlTiN-, and CrN/AlTiN-Coated DIN 1.2367 Hot Work Tool Steel

High Temperature Gas Nitridation and Wear Resistance of TiAl Based Alloys

The Effect of N Content on the Microstructure and Wear Resistance of Improved High-Carbon Chromium Bearing Steel

Martensitic Transformation Induced Planar Deformation of AlN Nanoprecipitates in High Nitrogen Stainless Steels

Effect of Plasma Nitriding Pretreatment on the Mechanical Properties of AlCrSiN-Coated Tool Steels

Enhancing Heavy Load Wear Resistance of AISI 4140 Steel Through the Formation of a Severely Deformed Compound-Free Nitrided Surface Layer

The Microstructure Transformations and Wear Properties of Nanostructured Bainite Steel with Different Si Content

Microstructures and Mechanical Performance of Plasma-Nitrided Al 0.3 CrFe 1.5 MnNi 0.5 High-Entropy Alloys

Improved high‐temperature softening resistance and wear resistance of AISI M42 high‐speed steel by N‐alloying

The Effects of Microstructure and Microtexture Generated During Solidification on Deformation Micromechanism in IN713C Nickel-Based Superalloy

Study of High-Strength Austenitic Nitrogen-Containing Steel Ingot Phase Formation and Structure

Finite Element and Experimental Analysis of Grain Refinement Caused by Dynamic Recrystallization During High-Speed Cutting of Nickel-Based Superalloys

Hardness Assessment Considering Nitrided Layers Based on Tempering Tests for Numerical Wear Prediction for Forging Processes

Prediction of contact stress and wear analysis of nitrided and CAPVD coated AISI H11 steel under dry sliding conditions

Mechanical behavior, tribological properties, and thermal stability of (AlCrNbSiTiVZr)N high entropy alloy nitride coatings and their application to Inconel 718 milling