Abstract:The aim of this study is to enhance the plasticity and strength of M2 high-speed steel through electron beam melting (EBM) technology. Therefore, by controlling different melting times to change the energy input, a gradient distribution of grain size and uniform distribution of carbides can be achieved. During the deformation process, the gradient structure causes geometrically necessary dislocations (GND) to accumulate near the boundary of regions in the soft zone, resulting in compressive stress in the soft zone and tensile stress in the hard zone, ultimately achieving heterogeneity-induced (HDI) work hardening. This study is to EBM technology for the design and fabrication of three types of M2 high-speed steel samples, denoted as SS-1, SS-2, and SS-3, utilizing three distinct scanning strategies: single melting, double melting, and a combination thereof. The microstructure and phase evolution of these samples were comprehensively characterized using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron backscatter diffraction (EBSD) techniques. The findings demonstrate that when sample SS-3 was subjected to the combined scanning strategy involving both single melting and double melting approaches, its crystal structure exhibited a gradient distribution along with the presence of back stress during tensile testing. Sample SS-3 achieved an average tensile strength of 1479 MPa with an average elongation rate of 1.8%. This represents an enhancement in average tensile strength by approximately 8.6% compared to sample SS-1 (∼1362 MPa) and a significant increase in average elongation rate by around 20% compared to SS-1 (∼1.44%). The gradient grain structure materials show the microstructure transformation from fine grain to coarse-grain in the same material, thus reducing the stress concentration caused by the change of mechanical properties in each region. The SS-3 sample can maintain significant ductility while improving tensile strength. Consequently, this represents a pivotal direction for the advancement of high-performance structural materials. The conducted experimental studies have demonstrated that geometrically necessary dislocations (GNDs) and their associated strain hardening play a crucial role in enhancing the strength of grain structure materials. Additionally, these are essential to achieve an exceptional synergy between strength and toughness in these materials.

Refinement of Eutectic Carbides in M2 High Speed Steel by Adjusting Magnetic Flux Density During Magnetic Controlled ESR Process

Morphology Refinement of Eutectic Carbides Assisted by Static Magnetic Field during Laboratory Electroslag Remelting Process

Effect of titanium and rare earth microalloying on microsegregation, eutectic carbides of M2 high speed steel during ESR process

Enhancement of removing inclusions from liquid melt film during the ESR process assisted by a static magnetic field

Effect of Secondary Aerosol Cooling on the Characteristics of Carbides in M42 High‐Speed Steel Produced by the Electroslag Remelting Withdrawal Process

Cleanliness improvement and microstructure refinement of H13 die steel by laboratory magnetic-controlled electroslag remelting

Study on Evolution Behavior of Carbides in Industrial‐Grade American Iron and Steel Institute M35 High‐Speed Steel Produced by Electroslag Remelting

Effect of Magnetic Field on Solidification Structure of A Centrifugal Cast High Speed Steel Roll

Microstructural evolution and tribological properties of M2 high-speed steel fabricated under various selective electron beam melting processing parameters

Improvement of mechanical property of M2 high-speed steel with hetero-microstructure tailored via electron beam melting

Effect of cerium on the primary carbides and inclusions in electroslag remelted M35 high speed steel

Evolutions of Microstructure by Cerium Treatment in As‐Cast M2 High‐Speed Steel

Microstructure and mechanical properties of M2 high speed steel produced by electron beam melting

Improvement of the Machining Characteristics in WEDM Based on Specific Discharge Energy and Magnetic Field–assisted Method

Effects of Static Magnetic Field on the Microstructure of Selective Laser Melted Inconel 625 Superalloy: Numerical and Experiment Investigations

Pronounced modification of the wetting and spreading behavior of molten Ag-Cu alloy on TC4 substrate in response to high magnetic fields

Control of Steel Composition and Evolution of Inclusions During Electroslag Remelting of NiCrMoV High‐Strength Steel

Magnetic field–assisted ultrasonic EDM removal mechanism and surface morphology study

Effect of Magnetic Field on Interfacial Energy and Precipitation Behavior of Carbides in Reduced Activation Steels

Effect of M-EMS current intensity on the subsurface segregation and internal solidification structure for bloom casting of 42CrMo steel

Rapid Solidification Microstructure and Carbide Precipitation Behavior in Electron Beam Melted High-Speed Steel