Effect of cerium on the primary carbides and inclusions in electroslag remelted M35 high speed steel

Dingli Zheng,Guojun Ma,Jing Li,Jung-wook Cho,Zhang Xiang,Mengke Liu,Junlin Zhu
DOI: https://doi.org/10.1016/j.jmrt.2023.05.044
IF: 6.267
2023-05-12
Journal of Materials Research and Technology
Abstract:To restrain the formation of primary carbides in M35 high speed steel, the present work investigated the effect of cerium on the microstructure, primary carbides and inclusions in electroslag remelted M35 high speed steel based on experimental characterizations and thermodynamic calculations. The primary carbides in M35 high speed steel are M 2 C-type carbides with orthorhombic crystal structure and MC-type carbides with FCC crystal structure. M 2 C-type carbides are the dominant carbides, whose precipitation is prior to the MC-type carbides. With adding cerium content to 0.0230wt%, the evolutionary process of inclusions is: MgO∙Al 2 O 3 →Ce 2 O 3 , CeAlO 3 and Ce 2 O 2 S→Ce 2 O 3 , Ce 2 O 2 S and Ce 2 O 3 core surrounded by Ce-As-P layer. Adding cerium content from 0 to 0.0230wt% causes the secondary dendrite arm spacing to decrease from 36.8 μm to 29.4 μm, as the heterogeneous nucleation of Ce 2 O 3 , Ce 2 O 2 S and CeAlO 3 inclusions, as well as the effect of dissolved cerium including the increase in the constitutional undercooling and the drag on the migration of liquid-solid interface. Ce 2 O 3 , Ce 2 O 2 S and CeAlO 3 are the less effective heterogeneous nucleation cores for M 2 C-type and MC-type primary carbides precipitation than MgO∙Al 2 O 3 inclusions, which is conducive to the decrease in the area fraction of primary carbides with adding 0.0067wt% cerium. Further increasing cerium content to 0.0230wt%, the formation of Ce-As-P inclusions surrounding Ce 2 O 3 promotes the precipitation of M 2 C-type primary carbides, causing the increase in the area fraction of primary carbides.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?