Abstract:Charge trap memory devices with Zr x Si1–x O2 films as charge trapping layer consisting of nine [(ZrO2) m (SiO2) n (ZrO2) m (SiO2) n ] units have been fabricated and investigated. The composition distribution was modulated by controlling the m and n values in each unit. It is observed that the variation of composition distribution can induce the energy band bending and additional potential barrier, which significantly improve the program/erase speed and data retention characteristics as well as extending the temperature insensitive range. When the effective potential barrier including classic potential barrier and additional potential barrier is 1.52 eV, the memory device exhibits a lower charge loss of 4.5% at 200 °C over a period of 104 s, a wider temperature insensitive range of 20 °C–111 °C, and a faster program time of 4.0 × 10−5 s achieving +6 V flat band voltage shift. The effective potential barrier values should be in the range of 1.52–1.36 eV, taking into consideration the trade-off between the retention and program/erase speed. The additional potential barrier can increase the electron tunneling distance in the directions of tunneling layer and blocking layer, giving rise to recapture process and temperature insensitive of retention characteristics. In addition, the additional potential barrier decreases the electron tunneling distance arriving trapping layer conduction band, improving the program speed. The results provide a reference to trapping layer composition distribution for future charge trap memory applications.

Impact of Band-Engineering to Performance of High- K Multilayer Based Charge Trapping Memory

Performance Improvement of Charge Trap Flash Memory by Using A Composition-Modulated High-K Trapping Layer

Performance Enhancement Of Multilevel Cell Nonvolatile Memory By Using A Bandgap Engineered High-Kappa Trapping Layer

The Interface Inter-Diffusion Induced Enhancement of the Charge-Trapping Capability in Hfo2/Al2o3 Multilayered Memory Devices

Band-Alignment Dominated Retention Behaviors In High-K Composite Charge-Trapping Memory Devices

The Dominant Factors Affecting the Memory Characteristics of (ta2o5)x(al2o3)1−x High-K Charge-Trapping Devices

Engineering Improvement of the Core Layers of Charge Trapping Flash Memory Based on Doped HfO2 and Segmented Fabrication

Study on the Charge Storage Characteristics of High-k(HfO_2)_(0.8)(Al_2O_3)_(0.2) Based Charge Trapping Memory Device

Performance of Nonvolatile Memory by Using Band-Engineered SrTiO3/HfON Stack As Charge-Trapping Layer

Improved Performances of Metal-Oxide-Nitride-Oxide-Silicon Memory with Hftion As Charge-Trapping Layer

Improved Memory Characteristics of A Novel TaN/Al2O3/TiO2/HfO2/SiO2/Si Structured Charge Trapping Memory

Improvement of the Charge Retention of a Non-Volatile Memory by a Bandgap-Engineered Charge Trap Layer

Coupling effects of interface charge trapping and polarization switching in HfO2-based ferroelectric field effect transistors

Visualization on Charge Distribution Behavior in Thickness-Scalable HfO2 Trapping Layer by In-Situ Electron Holography and Kelvin Probe Force Microscopy Technology

Process Optimization of HfAlO Trapping Layer for High Performance Charge Trap Flash Memory Application

Outstanding Memory Characteristics with Atomic Layer Deposited Ta2O5/Al2O3/TiO2/Al2O3/Ta2O5 Nanocomposite Structures As the Charge Trapping Layer

Effects of Composition on the Memory Characteristics of (Hfo2)x(al2o3)1-Xbased Charge Trap Nonvolatile Memory

Enhancement of the Charge Trapping Performances with HfAlO Composite Oxide Thin Films in SONOS-type Nonvolatile Memory

Correlation between memory characteristics and energy band bending resulted from composition distribution of trapping layer for charge trap memory

Effect of Pre-annealing to Blocking Oxide on the Performance of Dual Trapping-layer Engineered Charge Trapping Memory

The Effect of Thermal Treatment Induced Inter-Diffusion at the Interfaces on the Charge Trapping Performance of Hfo2/Al2o3 Nanolaminate-Based Memory Devices