Abstract:W70Cu30(W-30 wt.% Cu) alloys were fabricated using cold pressing and infiltration sintering methods from two types of powders, i.e., mixed copper-tungsten (M-Cu-W) powders and our newly developed copper-coated tungsten composite (Cu@W) powders. Microstructure, mechanical and arc-ablation properties of the W70Cu30 alloys were investigated, and the mechanism of enhanced physical/mechanical properties and arc-erosion resistance of the W70Cu30 alloys was discussed. For the W70Cu30 alloys prepared using the Cu@W powders, their physical properties, including hardness, electrical conductivity and relative density were much better than those prepared from the M-Cu-W powders. The W70Cu30 alloys fabricated from the Cu@W powders were free of cracks, and showed homogenous distributions of W and Cu network structures. Whereas for the alloys prepared from the M-Cu-W powders, segregation of Cu was observed and the segregation size was about 40-100 mm. Characterization of arc-erosion morphologies of the W70Cu30 alloys prepared with the Cu@W powders revealed the occurrence of evaporation of Cu phase; whereas that of W70Cu30 alloys prepared with the M-Cu-W powders revealed the occurrence of the sputtering of Cu. After arc breakdown for 200 times, mass loss of alloys made using the mixed powders was twice as much as those made using the coated composite powders. Based on the experimental results and theoretical analysis, an arc breakdown mechanism of the WCu-C alloys using the composite powders was proposed which is attributed to the formation of a homogeneous Cu-Cu network structure to uniformly disperse arc energy and dissipate the generated heat, thus prolonging the service life of the WCu alloy contacts. (c) 2017 Elsevier B.V. All rights reserved.

Infiltrated W–Cu Composites with Combined Architecture of Hierarchical Particulate Tungsten and Tungsten Fibers

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Insight into the Microstructure and Tensile Behavior of the W–Cu Composite Reinforced with Tungsten Fibers and Particulates

Infiltration Sintering of WCu Alloys from Copper-Coated Tungsten Composite Powders for Superior Mechanical Properties and Arc-Ablation Resistance

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Microstructure and properties of W Cu composites reinforced by in-situ generated WC

Microstructure and Mechanical Properties of W-WC/Fe Composite Fiber-Reinforced Fe Matrix Composite Prepared by Combination of Infiltration and In-Situ Solid Phase Diffusion

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration

Enhancing strength-ductility properties of immiscible W-Cu composite by creating low-energy phase interfaces

Multilayered W-Cu composites with enhanced strength, electrical conductivity and wear resistance

Freeze-casted tungsten skeleton reinforced copper matrix composites

Enhanced mechanical properties and thermal conductivity of W-30Cu composite fabricated with monodisperse and nearly spherical W powder

Fabrication and Microstructure of C/Cu Composites

Microstructure and Mechanical Properties of Intragranular W-Cu/TiC-ZrC Composite Prepared by Reactive Melt Infiltration at 1300 °C

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Preparation of Tungsten Fiber Reinforced-Tungsten/copper Composite for Plasma Facing Component

A novel approach to fabricate WC reinforced W Cu composites via MSC and infiltration method

Performance of a Hierarchically Nanostructured W–Cu Composite Produced via Mediating Phase Separation

Fabrication of W–Cu composites by microwave infiltration

W-ZrC composites prepared by reactive melt infiltration of Zr2Cu alloy into partially carburized W preforms