Abstract:Tungsten-copper (W-Cu) composites are used as high temperature frictional materials under special service conditions for electromagnetic gun rail and precision guide for rolled pieces due to their good ablation resistance and electrical conductivity. However, they have poor wear resistance at elevated temperatures. In this paper, surface carburization method was applied on the W-20 wt%Cu composite to investigate the mechanisms of carburization and its effects on the high temperature friction behavior of composite. Carburization process has been done at a temperature of 1100 degrees C for 30 h. The obtained results showed that carburizing at 1100 degrees C with a dwelling time of 30 h resulted into formation of a carburized layer and a dense intermediate sub-layer on the substrate. Also, the surface carburized layer with a thickness of about 70 pm composed of mixed phases of graphite, WC and W2C. The hardness of carburized layer (similar to HV454) was significantly higher than that of substrate (HV223). Also, bending strength of the carburized W-Cu composites has been significantly improved, although their electrical conductivity and tensile strength was decreased slightly. The carburization mechanism of the W-Cu composites was found to be dominant by carbon atom diffusion through reaction with W atoms and formation of surface liquid copper, which promoted migration and diffusion of tungsten and carbon at high temperatures. Average coefficients of friction and wear rate of carburized W-Cu composites are all lower than these of un-carburized W-Cu composites owing to the presence of surface carburized layer. Also, formation of CuWO4 at high temperatures reduced the friction and wear resistance of the W-Cu composites.

Preparation of Tungsten Fiber Reinforced-Tungsten/copper Composite for Plasma Facing Component

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Mechanical Properties of a Novel Tungsten Fiber-Reinforced Tungsten Composite Prepared Through Powder Extrusion Printing and High-Pressure High-Temperature Sintering

Interfacial Failure Mechanism in Tungsten Fiber Reinforced Copper-Based Composites Fabricated by Combustion Synthesis Melt Infiltration under Ultra-High Gravity

Modifying the Properties of Tungsten Based Plasma Facing Materials with Single-Wall Carbon Nanotubes

Progress in the development of industrial scale tungsten fibre-reinforced composite materials

Micro/Nano Composited Tungsten Material and Its High Thermal Loading Behavior

Infiltrated W–Cu Composites with Combined Architecture of Hierarchical Particulate Tungsten and Tungsten Fibers

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

Development of New Tungsten-based Materials as Plasma Facing Materials

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Tungsten-Copper Composite Fabricated by Hot-Shock Consolidation

Bonding Tungsten, W–Cu-alloy and Copper with Amorphous Fe–W Alloy Transition

Preparation and mechanical property of W f/Cu alloy matrix composites

Fabrication and Evaluation of Plasma-Sprayed Functionally Gradient W/Cu Coatings As Plasma Facing Materials in Fusion Devices

The Process of Surface Carburization and High Temperature Wear Behavior of Infiltrated W-Cu Composites

Design and Thermal Shock Performance of W/Cu Functionally Graded Material used as Plasma Facing Component

High Heat Flux Testing of Tungsten Plasma Facing Materials

Galvanic process for Cu-infiltration of W fibre-reinforced heat sinks

Coating Tungsten on C/C-Cu Composites Surface by Plasma Spraying

Preparation and Performance Analysis of Tungsten Wire-CVD Tungsten Composite Material