Abstract:The incongruent reactions between Zr-Cu melts and WC solid were studied. Mo was used as a tracer to track the movement of "heavy" W atoms during the incongruent reaction. In separate experiments, dense polycrystalline plates and porous preforms of W0.9Mo0.1C were reacted with Zr2Cu and Zr14Cu51 melts at 1200 °C, 1300 °C and 1600 °C for 15 minutes. The microstructure of the reactive interfaces was studied using scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectroscopy. The change of microstructure and chemical composition at the reactive interface was observed as a function of temperature, Zr content in the melt and radius of the W0.9Mo0.1C solid. When the Zr-Cu melts contact the W0.9Mo0.1C solid, W, Mo and C all dissolve in the melt. The precipitation of W and W2Zr is based on Zr activity in the Zr-Cu melt after a quick formation of ZrCx. Both the dissolution rate and the amount of WC solid increase with decreasing radius of the WC particles, increasing Zr content in the Zr-Cu melts, and increasing reaction temperature. If the dissolution rate of WC is fast enough and the WC particles are in small sizes, the dissolution-precipitation is the main aspect. If a continuous ZrC layer quickly forms to separate the WC solid from Zr-Cu melts. The reaction is, therefore, controlled by the diffusion of carbon through the W and/or ZrC layers.

W-ZrC composites prepared by reactive melt infiltration of Zr2Cu alloy into partially carburized W preforms

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

Ternary Phase Zr X Cu Y C Z in Reactively Infiltrated ZrC / W Composite

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Effect of ZrC nanopowder addition in WC preforms on microstructure and properties of W–ZrC composites prepared by the displacive compensation of porosity (DCP) method

Precipitations of W/Cu metallic phases in ZrC in the reactive melt infiltrated ZrC/W composite

In-situ fabrication and characterization of W-ZrC composites via pressureless reaction sintering

ZrC Modified Carbon/carbon Composites Using ZrSi2 and Zr-Cu Alloys As Reactive Infiltrating Materials: A Comparative Investigation

Microstructure and Ablation Behavior of W Coating Prepared by Atmospheric Plasma Spraying for Zr/Cu Infiltrated C/C Composites

Mechanism of Incongruent Reactions Between Zr-Cu Melts and Solid Tungsten Carbide

Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering

Correlation of C/C preform density and microstructure and mechanical properties of C/C-ZrC-based ultra-high-temperature ceramic matrix composites

Microstructure and flexural strength of C/HfC-ZrC-SiC composites prepared by reactive melt infiltration method

Spark plasma sintered WC-Ni cemented carbides with various contents of ZrC nano-powder

Fabrication and microstructure evolution of Csf/ZrB2-SiC composites via direct ink writing and reactive melt infiltration

Ultra-coarse cemented tungsten carbide with (Zr,W)C x precipitates in ceramic phase

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

Reactive sintering of 2.5D Cf/ZrC-SiC ceramic matrix composite

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration