Abstract:The incongruent reactions between Zr-Cu melts and WC solid were studied. Mo was used as a tracer to track the movement of "heavy" W atoms during the incongruent reaction. In separate experiments, dense polycrystalline plates and porous preforms of W0.9Mo0.1C were reacted with Zr2Cu and Zr14Cu51 melts at 1200 °C, 1300 °C and 1600 °C for 15 minutes. The microstructure of the reactive interfaces was studied using scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectroscopy. The change of microstructure and chemical composition at the reactive interface was observed as a function of temperature, Zr content in the melt and radius of the W0.9Mo0.1C solid. When the Zr-Cu melts contact the W0.9Mo0.1C solid, W, Mo and C all dissolve in the melt. The precipitation of W and W2Zr is based on Zr activity in the Zr-Cu melt after a quick formation of ZrCx. Both the dissolution rate and the amount of WC solid increase with decreasing radius of the WC particles, increasing Zr content in the Zr-Cu melts, and increasing reaction temperature. If the dissolution rate of WC is fast enough and the WC particles are in small sizes, the dissolution-precipitation is the main aspect. If a continuous ZrC layer quickly forms to separate the WC solid from Zr-Cu melts. The reaction is, therefore, controlled by the diffusion of carbon through the W and/or ZrC layers.

Ternary Phase Zr X Cu Y C Z in Reactively Infiltrated ZrC / W Composite

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Precipitations of W/Cu metallic phases in ZrC in the reactive melt infiltrated ZrC/W composite

Evolution of Phase, Microstructure and ZrC Lattice Parameter in Solid-solution-treated W-ZrC Composite

Microstructure and Mechanical Properties of Intragranular W-Cu/TiC-ZrC Composite Prepared by Reactive Melt Infiltration at 1300 °C

Microstructural Analysis Of A C-F/Zrc Composites Produced By Melt Infiltration

Microstructure and Mechanical Properties of ZrC x -NbC y -Cu Composites by Reactive Infiltration at 1 300 °C

Microstructure and Properties of ZrC–W Composite Fabricated by Reactive Infiltration of Zr2Cu into WC/W Preform

Phase Field Simulation of the Phase Separation in the TiC-ZrC-WC System

Processing of ZrC-W composites produced by reactive melt infiltration method

W-ZrC composites prepared by reactive melt infiltration of Zr2Cu alloy into partially carburized W preforms

Evaluation of phase relationship in W-Fe-C ternary system through symmetry principles and first-principles calculation

Mechanism of Incongruent Reactions Between Zr-Cu Melts and Solid Tungsten Carbide

Design, Synthesis, Structure, and Stability of Novel Multi-Principal Element (ti,zr,hf,w)c Ceramic with a Miscibility Gap

Phase, microstructure and property evolutions of reactively synthesized YSZ-ZrC composite coating based on the content regulation of the precursor

Microstructural Characterization of a Cf/ZrC Composite Manufactured by Reactive Melt Infiltration

Microstructure and Mechanical Properties of Mo-ZrC-Cu Composites Synthesized by Reactive Melt Infiltration of Zr-Cu Melt into Porous Mo2C Preforms at 1300 °C

Ultra-coarse Cemented Tungsten Carbide with (zr,w)cx Precipitates in Ceramic Phase

The Phase Decomposition in Non-Equimolar (zrhfvnbmow)cx Complex Concentrated Carbides Via Carbon Content Regulation

Reactive wetting and infiltration of polycrystalline WC by molten Zr2Cu alloy

Analysis of phases in a Cu–Cr–Zr alloy