Tracking the evolution of microstructure and phases of WCoB-Co cermets during sintering
Cunhui Yuan,Haiqing Yin,Guoqiang Yang,Xin Yang,Bin Xu,Zhenghua Deng,Yangfan Liu,Wei Li,Cong Zhang,Ruijie Zhang,Xuanhui Qu
DOI: https://doi.org/10.1016/j.ijrmhm.2021.105550
IF: 4.804
2021-08-01
International Journal of Refractory Metals and Hard Materials
Abstract:<p>Transition metal boride enable applications in fields of cutting tools as the hard phase, but their fabrication suffers from shortcomings in high temperature for binary and hard/soft phase balance. Here, we leveraged a WCoB-Co cermets prepared by using elemental powders of W, Co and B powders via in situ synthesis method and investigated the microstructure evolution of a composite structure of WCoB/Co. The phase evolution, microstructure evolution and mechanical properties were investigated using X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). The complete sintering process consist of three solid-phase reaction stages and one liquid-phase sintering stage. The solid-phase reaction stage includes the following three reactions: B + 2Co → Co<sub>2</sub>B, 11 W +15 Co<sub>2</sub>B → 9WCoB + W<sub>2</sub>Co<sub>21</sub>B<sub>6</sub>, and 14 W + 2W<sub>2</sub>Co<sub>21</sub>B<sub>6</sub> → 12WCoB + 23Co + Co<sub>7</sub>W<sub>6</sub>. The eutectic liquid phase, essential for the densification, forms at 1323 °C. The Rockwell hardness and density value reach 87.5HRA and 12.11 g/cm<sup>3</sup>, respectively. At 1380 °C, the traverse rupture strength (TRS) reaches the peak value of 1495 MPa. Moreover, the results show that transgranular fracture is the main fracture mode. The densification stage was completed at ~1400 °C. In particular, Co<sub>7</sub>W<sub>6</sub> phase was discovered during the study of the evolution of WCoB-Co cermets. An increase of the B content was found to be beneficial to eliminate the Co<sub>7</sub>W<sub>6</sub> phase that proved to be detrimental to mechanical properties.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering