Abstract:In this study, WC-12Co cemented carbides were prepared by laser powder bed fusion (LPBF) on a WC-20Co substrate. The effects of the scanning speed and the substrate on the microstructure, mechanical properties and wear characteristics of the WC-12Co cemented carbide were investigated. The results showed that an alternating distribution of coarse and fine WC grains is observed in the LPBF-prepared WC-12Co cemented carbides. As the laser scanning speed decreases or the laser energy density increases, the WC phase gradually decomposes, accompanied by the loss of C and the formation of ƞ phases. WC-12Co cemented carbides produced at a lower scanning speed exhibit a higher density of thermal cracks, while those produced at a higher scanning speed have a larger number of pores. As the laser scanning speed increases, the transverse rupture strength (TRS) first increases to a maximum value of 823.13 MPa and then decreases. The variation of TRS is mainly attributed to the evolution of the brittle ƞ-phase and metallurgical defects. For WC-12Co cemented carbides formed at low scanning speeds, the brittle η-phase may fracture and cut through the matrix during the friction process, leading to an increase in coefficient of friction (COF) and wear mass loss. For samples formed at high scanning speeds, the formation and detachment of the shear layer could accelerate the friction process and undermine the wear resistance of the WC-12Co cemented carbide. Therefore, the sample prepared at the scanning speed of 400 mm/s shows the best wear performance.

Ultra-coarse cemented tungsten carbide with (Zr,W)C x precipitates in ceramic phase

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Microstructure and mechanical properties of WC–Co-based cemented carbide with bimodal WC grain size distribution

Precipitations of W/Cu metallic phases in ZrC in the reactive melt infiltrated ZrC/W composite

High temperature fracture mechanism of ultrafine WC-Co cemented carbides containing (Ti,W)C

Novel WC-Co-Ti3SiC2 cemented carbide with ultrafine WC grains and improved mechanical properties

Spark plasma sintered WC-Ni cemented carbides with various contents of ZrC nano-powder

Enhanced Coarse-Grained WC-Co(Ce) Cemented Carbide Prepared through Co-Precipitation

Coprecipitation of co and La 2 O 3 coprecipitation on WC for tailoring the grain distribution and boundary of high-performance coarse-grained WC-10Co cemented carbide

Ultrafine/nano WC-Co Cemented Carbide: Overview of Preparation and Key Technologies

The influence of Ti-induced precipitates on the microstructure and mechanical properties of (Zr,W)C solid solution

Microstructure and mechanical properties of WC-12Co cemented carbide fabricated by laser powder bed fusion on a WC-20Co cemented carbide substrate

Ultrafine grained WC-10FeCoCu cemented carbides doped with La 2 O 3 prepared by spark plasma sintering

Study on preparation and properties of WC-8Co cemented carbide doped with rare earth oxide

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

Effect of carbon content on the properties of inhomogeneous cemented carbides with fine-grained structures produced via one-step transformation

Synthesis and characterization of high-entropy carbide dispersed strengthening tungsten: Mechanical and thermal properties analysis