Abstract:The incongruent reactions between Zr-Cu melts and WC solid were studied. Mo was used as a tracer to track the movement of "heavy" W atoms during the incongruent reaction. In separate experiments, dense polycrystalline plates and porous preforms of W0.9Mo0.1C were reacted with Zr2Cu and Zr14Cu51 melts at 1200 °C, 1300 °C and 1600 °C for 15 minutes. The microstructure of the reactive interfaces was studied using scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectroscopy. The change of microstructure and chemical composition at the reactive interface was observed as a function of temperature, Zr content in the melt and radius of the W0.9Mo0.1C solid. When the Zr-Cu melts contact the W0.9Mo0.1C solid, W, Mo and C all dissolve in the melt. The precipitation of W and W2Zr is based on Zr activity in the Zr-Cu melt after a quick formation of ZrCx. Both the dissolution rate and the amount of WC solid increase with decreasing radius of the WC particles, increasing Zr content in the Zr-Cu melts, and increasing reaction temperature. If the dissolution rate of WC is fast enough and the WC particles are in small sizes, the dissolution-precipitation is the main aspect. If a continuous ZrC layer quickly forms to separate the WC solid from Zr-Cu melts. The reaction is, therefore, controlled by the diffusion of carbon through the W and/or ZrC layers.

Precipitations of W/Cu metallic phases in ZrC in the reactive melt infiltrated ZrC/W composite

Ternary Phase Zr X Cu Y C Z in Reactively Infiltrated ZrC / W Composite

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Mechanism of Incongruent Reactions Between Zr-Cu Melts and Solid Tungsten Carbide

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Ultra-coarse cemented tungsten carbide with (Zr,W)C x precipitates in ceramic phase

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

The influence of Ti-induced precipitates on the microstructure and mechanical properties of (Zr,W)C solid solution

Microstructure and phase components of the as-cast Cu-0.4%Cr-0.12%Zr-0.01%Si

Microstructure and Ablation Behavior of W Coating Prepared by Atmospheric Plasma Spraying for Zr/Cu Infiltrated C/C Composites

Microstructural Analysis Of A C-F/Zrc Composites Produced By Melt Infiltration

Role of Zr in Cu-rich single-phase and nanocomposite Cu-Zr: molecular dynamics and experimental study

Understanding wetting mechanism of pure Cu on C/C composites modified by chromium carbide

Microstructural Characterization of a Cf/ZrC Composite Manufactured by Reactive Melt Infiltration

In-situ fabrication and characterization of W-ZrC composites via pressureless reaction sintering

Mechanical and tribological properties of WC particles reinforced Cu-20Zn matrix composites

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Formation mechanism of composite secondary phase particles in a solution-treated Si-modified Zircaloy-4

Novel synthesis of CuW composite reinforced with lamellar precipitates via aluminothermic reduction

Fine precipitation scenarios of AlZnMg(Cu) alloys revealed by advanced atomic-resolution electron microscopy study Part I: Structure determination of the precipitates in AlZnMg(Cu) alloys

Microstructure and properties of W Cu composites reinforced by in-situ generated WC