Mechanism of Incongruent Reactions Between Zr-Cu Melts and Solid Tungsten Carbide

Dong Wang,Yujin Wang

DOI: https://doi.org/10.1007/s11663-020-01846-4

2020-05-06

Metallurgical and Materials Transactions B

Abstract:<p class="a-plus-plus">The incongruent reactions between Zr-Cu melts and WC solid were studied. Mo was used as a tracer to track the movement of "heavy" W atoms during the incongruent reaction. In separate experiments, dense polycrystalline plates and porous preforms of W<sub class="a-plus-plus">0.9</sub>Mo<sub class="a-plus-plus">0.1</sub>C were reacted with Zr<sub class="a-plus-plus">2</sub>Cu and Zr<sub class="a-plus-plus">14</sub>Cu<sub class="a-plus-plus">51</sub> melts at 1200 °C, 1300 °C and 1600 °C for 15 minutes. The microstructure of the reactive interfaces was studied using scanning electron microscopy, transmission electron microscopy and energy-dispersive X-ray spectroscopy. The change of microstructure and chemical composition at the reactive interface was observed as a function of temperature, Zr content in the melt and radius of the W<sub class="a-plus-plus">0.9</sub>Mo<sub class="a-plus-plus">0.1</sub>C solid. When the Zr-Cu melts contact the W<sub class="a-plus-plus">0.9</sub>Mo<sub class="a-plus-plus">0.1</sub>C solid, W, Mo and C all dissolve in the melt. The precipitation of W and W<sub class="a-plus-plus">2</sub>Zr is based on Zr activity in the Zr-Cu melt after a quick formation of ZrC<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub>. Both the dissolution rate and the amount of WC solid increase with decreasing radius of the WC particles, increasing Zr content in the Zr-Cu melts, and increasing reaction temperature. If the dissolution rate of WC is fast enough and the WC particles are in small sizes, the dissolution-precipitation is the main aspect. If a continuous ZrC layer quickly forms to separate the WC solid from Zr-Cu melts. The reaction is, therefore, controlled by the diffusion of carbon through the W and/or ZrC layers.</p>