Abstract:Herein, ZrC coating was fabricated on the surface of zirconium via interstitial carburization. High-carbon steel was selected as the carbon source to supply the interstitial carbon atoms and was hot-pressed with zirconium substrate at 1150 degrees C and uniaxial pressure of 2 MPa. The interstitial carbon atoms diffused into the surface of Zr forming a ZrC coating. The microstructure of the coating was characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron backscattered diffraction (EBSD). The obtained coating was completely dense and pure ceramic, consisting of a single ZrC phase with a volume fraction of 100%. The diameter of ZrC grains exhibited a gradient distribution with a range of 180 nm to 5.9 mu m. The thickness of the coating was proportional to the square root of the carburizing time, following the classical parabolic law, reaching a coating thickness of 7.2 mu m after carburizing for 10 h. The microhardness tested on the coating surface reached 1500 HV and nanohardness measured on the cross-section of the ZrC coating reached 27 GPa, displaying a remarkable improvement compared to the zirconium substrate (192 HV and 3.6 GPa). The average fracture toughness of ZrC coating measured via Vickers indentation was 1.9 MPa.m(1/2). In response to a scratch where the scratch load increased linearly from 0 to 100 N, the coating demonstrated excellent adhesion with the substrate. As per the obtained results, we expect that the interstitial carburization method can also be applied to various Zr-based alloys. (C) 2020 Elsevier B.V. All rights reserved.

Microstructural Characterization of a Cf/ZrC Composite Manufactured by Reactive Melt Infiltration

Microstructural development of a Cf/ZrC composite manufactured by reactive melt infiltration

Microstructural Analysis Of A C-F/Zrc Composites Produced By Melt Infiltration

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Ternary Phase Zr X Cu Y C Z in Reactively Infiltrated ZrC / W Composite

Reaction mechanism and microstructure development of ZrSi2 melt-infiltrated Cf/SiC-ZrC-ZrB2 composites: The influence of preform pore structures

Influence of Reactive Melt Infiltration Parameters on Microstructure and Properties of Low Temperature Derived Cf/ZrC Composites

3D microstructure characterization of 2D Cf-ZrB2-SiC ultra-high temperature ceramic matrix composites using X-ray microscopy

Fabrication and properties of Cf/ZrC‐SiC‐based composites by an improved reactive melt infiltration

A study of interface reaction zone in a SiC fibre/Ti-17 composite

Microstructure and flexural strength of C/HfC-ZrC-SiC composites prepared by reactive melt infiltration method

Microstructure and Mechanical Properties of ZrC x -NbC y -Cu Composites by Reactive Infiltration at 1 300 °C

Interphase Degradation of Three‐dimensional Cf/SiC–ZrC–ZrB2 Composites Fabricated Via Reactive Melt Infiltration

Microstructure and Properties of ZrC–W Composite Fabricated by Reactive Infiltration of Zr2Cu into WC/W Preform

Microstructure and Mechanical Properties of Intragranular W-Cu/TiC-ZrC Composite Prepared by Reactive Melt Infiltration at 1300 °C

Zirconia Reinforced Reaction Bonded Silicon Carbide Composites: Microstructure and Mechanical Properties

Microstructure Characterization by X-Ray Computed Tomography of C/C-SiC Ceramic Composites Fabricated with Different Carbon Fiber Architectures

Fabrication and microstructure evolution of Csf/ZrB2-SiC composites via direct ink writing and reactive melt infiltration

Influence of ZrC on the Microstructure of Its Surrounding Resin-Based Carbon at High Temperature

Microstructure and Mechanical Properties of ZrC Coating on Zirconium Fabricated by Interstitial Carburization

Microstructure and Mechanical Properties of Mo-ZrC-Cu Composites Synthesized by Reactive Melt Infiltration of Zr-Cu Melt into Porous Mo2C Preforms at 1300 °C