Experimental determination of the phase equilibria in the Co–Fe–Zr ternary system
C.P. Wang,Y. Yu,H.H. Zhang,H.F. Hu,X.J. Liu
DOI: https://doi.org/10.1016/j.jallcom.2011.01.030
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Research highlights ► We determined four isothermal sections of the Co–Fe–Zr system from 1000 °C to 1300 °C. ► No ternary compound was found in the Co–Fe–Zr ternary system. ► The solubility of Fe in the liquid phase at 1300 °C is extremely large. ► The (Co, Fe) 2 Zr phase form the continuous solution from Co–Zr side to Fe–Zr side. ► The solubility of Zr in the fcc (Co, Fe) phase is extremely small. Abstract The phase equilibria in the Co–Fe–Zr ternary system were investigated by means of optical microscopy (OM), electron probe microanalysis (EPMA), X-ray diffraction (XRD), and differential scanning calorimetry (DSC) on equilibrated ternary alloys. Four isothermal sections of the Co–Fe–Zr ternary system at 1300 °C, 1200 °C, 1100 °C and 1000 °C were experimentally established. The experimental results indicate that (1) no ternary compound was found in this system; (2) the solubility of Fe in the liquid phase of the Co-rich corner at 1300 °C is extremely large; (3) the liquid phase in the Zr-rich corner and the (Co,Fe) 2 Zr phase form the continuous solid solutions from the Co–Zr side to the Fe–Zr side; (4) the solubility of Zr in the fcc (Co, Fe) phase is extremely small. Keywords Metal and alloys Phase diagrams X-ray diffraction 1 Introduction The Co–Fe base alloys are important magnetic materials in applications of electronic industry, information technology and recording media [1,2] . The Co–Fe–Zr system is one of important subsystems for the typical magnetic metallic materials. In addition, the Co–Fe–Zr base alloys are also used as high temperature materials and amorphous materials [3–5] . For the advanced development of high-performance Co–Fe–Zr base alloys, accurate information on the phase equilibria in the Co–Fe–Zr system is especially required. Although the isothermal sections at 500 °C investigated by Mishenina et al. [6] and at 1000 °C determined by Raghavan [7] were available, however, there are still two main conflicts in the isothermal section at 1000 °C (shown in Fig. 1 ), which are summarized as follows: (1) the existence of the FeZr 2 phase at 1000 °C is obviously not in accordance with that in the Fe–Zr binary phase diagram (presented in Fig. 2 ) reviewed by Okamoto [8] and (2) the chemical compositions of the Fe 3 Zr phase has a big difference from that in Ref. [8] . Therefore, it is important and necessary to comprehensively determine the phase equilibria in the Co–Fe–Zr ternary system. In the Co–Fe–Zr ternary system, the Co–Fe [9] , Co–Zr [10–12] and Fe–Zr [8] three sub-binary systems have been experimentally investigated. The Co–Fe phase diagram is characterized by an extremely narrow solidification range. The fcc continuous solid solution exists from the fcc (Fe) phase to the fcc (Co) phase over a wide range of temperature [9] . In the Co–Zr phase diagram, there are five intermediate phases: Co 11 Zr 2 , Co 23 Zr 6 , Co 2 Zr, CoZr and CoZr 2 [10] . Later, Bataleva et al. [11] confirmed the existence of the CoZr 3 phase. Among these, Co 2 Zr and CoZr 3 phases have a range of homogeneity. The main information of the Co–Zr phase diagram is obtained by Pechin et al. [10] and our work [12] . The Fe–Zr system reviewed by Okamoto [8] shows that the stable phases are the liquid phase, terminal solid solutions δFe, αFe, γFe, βZr, and αZr, and four intermetallic compounds, namely, Fe 23 Zr 6 , Fe 2 Zr, FeZr 2 , and FeZr 3 phases. Nine invariant reactions exist in the system involving all the phases mentioned above. The phase diagram in the Co–Fe [9] , Co–Zr [10] and Fe–Zr [8] three sub-binary systems are shown in Fig. 2 . The information of the stable solid phases in the three binary systems mentioned above is summarized in Table 1 . Recently, our group has been focused on developing a thermodynamic database of the phase diagrams in the Co-based alloys [13–21] . In order to obtain the detailed information of phase equilibria for the thermodynamic assessment, the objective of the present work is to experimentally determine the isothermal sections at 1300 °C, 1200 °C, 1100 °C and 1000 °C using the equilibrated ternary alloys, which will meet the need for the thermodynamic description of the Co–Fe–Zr ternary system and provide a better understanding of microstructures of promising alloys for practical applications. 2 Experimental procedure Cobalt (99.8 wt.%), iron (99.9 wt.%) and zirconium (99.7 wt.%) were used as starting materials. Bulk buttons were prepared from pure elements by arc melting under high purity argon atmosphere using a non-consumable tungsten electrode. The ingots were melted at least five times in order to achieve their homogeneity. The sample weight is around 20 g and the weight loss during melting is generally less than 0.20% of the sample weight. Afterwards, the ingots were cut into small pieces for heat treatments and further observations. The specimens were wrapped in Mo foil in order to prevent direct contact with the quartz ampoule, and put into quartz evacuated and backfilled with argon gas. The specimens were annealed in temperature range between 1000 °C and 1300 °C, respectively. The time of the heat treatment varied from several hours to 3 months depending on temperature and composition of the specimen. At the end of the heat treatment, the specimens were quenched into ice water. After standard metallographic preparation, the microstructural observations were carried out by optical microscopy (OM) and scanning electron microscopy (SEM). The reliable equilibrium compositions of each phase were determined by electron probe microanalysis (EPMA) (JXA-8100R, JEOL, Japan) based on the wavelength dispersive spectroscopy (WDS) and pure elements cobalt, iron and zirconium were used as standard materials. The conditions of measurements were 20.0 kV for voltage and 10 nA for beam current, respectively. The equilibrium compositions were obtained by averaging the compositions determined by EPMA. The X-ray diffraction (XRD) was used to identify the crystal structure of the constituent phases. The X-ray powder diffraction patterns of the experimental samples were carried out on a Phillips Panalytical X-pert diffractometer using Cu Kα radiation at 40 kV and 30 mA. The data were collected in the range of 2 θ from 20° to 90° at a step width of 0.0167°. The differential scanning calorimetry (DSC) method was used to determine the temperature of phase transformation. Al 2 O 3 power was used as reference substance. The heating and cooling rates were both set to 10 °C/min. All measurements were conducted under argon atmosphere. 3 Results and discussion 3.1 Microstructure The BSE (back-scattered electron) images of the typical ternary alloys for the Co–Fe–Zr system are presented in Fig. 3 (a)–(h). Phase identification was based on equilibrium composition measured by EPMA. The Co 80 Fe 13 Zr 7 (at.%) and Co 50 Fe 10 Zr 40 (at.%) alloys annealed at 1300 °C for 1 h and 6 days are respectively located in the two-phase regions (liquid + fcc (Co, Fe)) and (CoZr + (Co,Fe) 2 Zr), as characterized in Fig. 3 (a) and (b), respectively. The fcc (Co, Fe) phase and the (Co,Fe) 2 Zr phase distribute in the matrix of the liquid phase and CoZr phase, respectively. In the Co 87 Fe 6 Zr 7 (at.%) alloy quenched from 1200 °C, the two phases Co 11 Zr 2 and fcc (Co, Fe) were identified, as shown in Fig. 3 (c). The three-phase equilibrium of the liquid + (Co,Fe) 2 Zr + CoZr were identified in the Co 30 Fe 20 Zr 50 (at.%) alloys quenched from 1200 °C for 6 h, as indicated in Fig. 3 (d). The Co 40 Fe 45 Zr 15 (at.%) and Co 35 Fe 3 Zr 62 (at.%) annealed at 1100 °C for 3 months are located in the three-phase region of the Fe 23 Zr 6 + fcc (Co, Fe) + (Co,Fe) 2 Zr and two-phase region of the CoZr + CoZr 2 , as shown in Fig. 3 (e–f). In addition, the two-phase equilibrium of the (Co,Fe) 2 Zr + CoZr 2 and three-phase equilibrium of the CoZr 2 + (Co,Fe) 2 Zr + CoZr were identified in the Co 12 Fe 38 Zr 50 (at.%) and Co 25 Fe 30 Zr 45 (at.%) alloys annealed at 1000 °C for 4 months, respectively, and indicated in Fig. 3 (g) and (h), respectively. 3.2 Structure and melting points The Co 50 Fe 10 Zr 40 (at.%) alloy annealed at 1300 °C for 6 days was substantiated by the XRD experiment, as shown in Fig. 4 (a), where the characteristic peaks of the (Co,Fe) 2 Zr and CoZr phases are well distinguished by different symbols, which are consistent with the results determined by EPMA, as shown in Fig. 3 (b). In addition, the XRD result of Co 25 Fe 30 Zr 45 (at.%) alloy quenched from 1000 °C is shown in Fig. 4 (b), where the characteristic peaks of the CoZr, CoZr 2 and (Co,Fe) 2 Zr were marked by different symbols, which is observed in Fig. 3 (h). The DSC analysis was performed in order to determined the melting points of three different alloys Co 6 Fe 19 Zr 75 (at.%), Co 12 Fe 13 Zr 75 (at.%) and Co 19 Fe 6 Zr 75 (at.%). Their DSC curves on heating are presented in Fig. 5 , respectively. It can be known that the appearance of the liquid phase in the Zr-rich corner is below 1000 °C, which indicates that there should be a liquid phase from Co–Zr side to Fe–Zr side at 1000 °C. 3.3 Isothermal section The equilibrium compositions of the Co–Fe–Zr ternary system at 1300 °C, 1200 °C, 1100 °C and 1000 °C determined by EPMA are listed in Tables 2–5 , respectively. Based on these experimental data mentioned above, the isothermal sections at 1300 °C, 1200 °C, 1100 °C and 1000 °C were constructed in Fig. 6 (a)–(d). Fig. 6 (a) shows the isothermal section at 1300 °C, where the solubility of Zr in the fcc (Co, Fe) phase is extremely small and the solubility of Fe in liquid phase of the Co-rich corner is extremely large. In addition, the liquid phase in the Zr-rich corner and the (Co,Fe) 2 Zr phase form the continuous solid solutions from the Co–Zr side to the Fe–Zr side. The three-phase equilibrium (CoZr + (Co,Fe) 2 Zr + liquid), rather than ternary compound was identified. Three three-phase equilibria, fcc (Co, Fe) + liquid + Fe 23 Zr 6 , liquid + (Co,Fe) 2 Zr + Fe 23 Zr 6 and liquid + (Co,Fe) 2 Zr + Co 23 Zr 6 , as shown in Fig. 5 (a) in dashed lines, were still not determined. In the isothermal section at 1200 °C ( Fig. 6 (b)), two three-phase equilibria, CoZr + (Co,Fe) 2 Zr + liquid and fcc (Co, Fe) + (Co,Fe) 2 Zr + Fe 23 Zr 6 were determined. The solubility of Zr in the Co 23 Zr 6 phase is larger than that in the Co 11 Zr 2 phase. The liquid phase in the Co-rich corner disappears, but the liquid phase in the Zr-rich corner still form the continuous solid solutions from the Co–Zr side to the Fe–Zr side. As shown in Fig. 6 (c), the solid CoZr 2 phase, existing only below 1200 °C in the Co–Zr binary system [10–12] , appears in the isothermal section at 1100 °C. The solubility of Fe in the CoZr 2 phase was found to be extremely large. Three three-phase equilibria, CoZr + (Co,Fe) 2 Zr + CoZr 2 , fcc (Co, Fe) + (Co,Fe) 2 Zr + Fe 23 Zr 6 and fcc (Co, Fe) + Co 11 Zr 2 + Co 23 Zr 6 were determined and three three-phase equilibria shown in dashed line were still not determined. In the isothermal section at 1000 °C ( Fig. 6 (d)), the liquid phase was found to still exist in the Zr-rich corner and formed the continuous solutions from the Co–Zr side to Fe–Zr side, which also corresponds to the results of DSC analysis mentioned above, showing that the temperature of liquid phase of the Zr-rich corner appears at about 985 °C. The isothermal section at 1000 °C determined in present work is different from 1000 °C investigated by Raghavan [7] ( Fig. 1 ). In the present work, the melting point of the FeZr 2 phase was determined to be about 955.6 °C, which indicated that the FeZr 2 phase does not exist at 1000 °C. Thus, the continuous solid solution of (Co,Fe)Zr 2 phase does not exist at 1000 °C. 4 Conclusions Four isothermal sections of the Co–Fe–Zr ternary system at 1300 °C, 1200 °C, 1100 °C and 1000 °C were experimentally determined using equilibrated ternary alloys. The obtained experimental results show that: (1) the solubility of Fe in liquid phase of Co-rich corner at 1300 °C is extremely large; (2) the liquid phase of Zr-rich corner and the (Co,Fe) 2 Zr phase form the continuous solid solutions from the Co–Zr side to the Fe–Zr side; (3) the solubility of Zr in fcc (Co, Fe) phase is extremely small; (4) no ternary compound was found in this system. The newly determined phase equilibria of the Co–Fe–Zr ternary system will provide additional support for the thermodynamic assessment of this system in the underway work and practical application for the amorphous alloys. Acknowledgements This work was supported by the National Natural Science Foundation of China (Grant Nos. 51031003, 50771088, 50971109), the Ministry of Science and Technology of China (Grant Nos. 2009DFA52170 and 2009AA03Z101). The Support from Fujian Provincial Department of Science & Technology (Grant No. 2009I0024), Xiamen City Department of Science & Technology (Grant No. 3502Z20093001), and Aviation Science Fund (Grant No. 2009ZF68010) are acknowledged. References [1] V.K. Dugaev Y. Vygranenko M.M. Vieira Physica E 16 2003 558 562 [2] R.C. Sousa I.L. Prejbeanu C. R. Phys. 6 2005 1013 1021 [3] M. Zatroch P. Petrovič I. Brovko T. Švec M. Konč J. Magn. Magn. Mater. 112 1992 334 336 [4] L. Peng Q.H. Yang H.W. Zhang G.L. Xu M. Zhang J.D. Wang J. Rare Earths 26 2008 378 382 [5] R.Z. Gong X. Wang W.M. Cheng X. Shen Mater. Lett. 62 2008 266 268 [6] I.V. Mishenina E.F. Kazakova E.M. Sokolovskaya N.Y. Tolmacheva Moscow Univ. Chem. Bull. 51 1996 52 54 [7] V. Raghavan Ind. Inst. Met. 6 1992 681 686 [8] H. Okamoto J. Phase Equilib. 14 1993 652 653 [9] I. Ohnuma H. Enoki O. Ikeda R. Kainuma H. Ohtani B. Sundman K. Ishida Acta Mater. 50 2002 379 [10] W.H. Pechin D.E. Williams W.L. Larsen Trans. ASM 57 1964 464 473 [11] S.K. Bataleva V.V. Kuprina V.V. Burnasheva V.Y. Markiv G.N. Ronami S.M. Kurnetsova Moscow Univ. Chem. Bull. 25 1970 33 36 [12] X.J. Liu H.H. Zhang C.P. Wang K. Ishida J. Alloys Compd. 482 2009 99 105 [13] C.P. Wang X.J. Liu I. Ohnuma R. Kainuma K. Ishida J. Alloys Compd. 438 2007 129 141 [14] C.P. Wang J. Wang X.J. Liu I. Ohnuma R. Kainuma K. Ishida J. Alloys Compd. 453 2008 174 179 [15] C.P. Wang P. Yu X.J. Liu I. Ohnuma R. Kainuma K. Ishida J. Alloys Compd. 457 2008 150 156 [16] X.J. Liu P. Yu C.P. Wang K. Ishida J. Alloys Compd. 466 2008 169 175 [17] Y. Yu C.P. Wang X.J. Liu I. Ohnuma R. Kainuma K. Ishida Intermetallics 16 2008 1199 1205 [18] J. Wang X.J. Liu C.P. Wang J. Nucl. Mater. 374 2008 76 89 [19] C.P. Wang J. Wang S.H. Guo X.J. Liu I. Ohnuma R. Kainuma K. Ishida Intermetallics 17 2009 642 650 [20] C.P. Wang A.Q. Zheng X.J. Liu K. Ishida J. Alloys Compd. 478 2009 197 201 [21] X.J. Liu Z.P. Jiang C.P. Wang K. Ishida J. Alloys Compd. 478 2009 287 296