Abstract:In this study, C/C–SiC and C/C–SiC–ZrC composites were prepared via chemical vapor infiltration and polymer infiltration pyrolysis, and the ablation mechanism under hypersonic oxygen-rich environmental conditions was investigated. The C/C–SiC composites demonstrate an excellent ablation resistance in a hypersonic oxygen-rich environment with a relatively low temperature and speed of approximately 1800 K and 1100 m/s, respectively. It is only in the ablation center area with higher temperatures that a certain degree of thermochemical ablation was observed. The mass and linear ablation rates of C/C–SiC composites (0.027 g/s and 0.117 mm/s, respectively) showed a significant increase in a hypersonic oxygen-rich environment with a temperature and velocity of approximately 2050 K and 2000 m/s, respectively. The high-temperature ablation resistance of ZrC-modified C/C–SiC–ZrC composites improved significantly. However, the ZrC ceramic component had a considerable impact on the ablation resistance of the material. The structural integrity of C/C–20SiC–30ZrC composites was relatively high in hypersonic oxygen-rich environments with a jet temperature and velocity of 2050 K and 2000 m/s, respectively, and mass and linear ablation rates were 0.012 g/s and 0.015 mm/s, respectively. When the ZrC content increased by 40%, the ablation resistance of the composite reduced significantly, whereas the mass and linear ablation rates increased to 0.043 g/s and 0.130 mm/s, respectively.

ZrC Modified Carbon/carbon Composites Using ZrSi2 and Zr-Cu Alloys As Reactive Infiltrating Materials: A Comparative Investigation

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Construction of sandwich-structured C/C-SiC and C/C-SiC-ZrC composites with good mechanical and anti-ablation properties

Enhanced ablative resistance of C/C composites with densified ZrB 2 -based ceramics by incorporation of Mo as interface layer

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

The mechanical properties of C/C-ZrC-SiC composites after laser ablation

Microstructure and flexural strength of C/HfC-ZrC-SiC composites prepared by reactive melt infiltration method

Ablation of advanced C/C-ZrC-SiC leading edge composites

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Comparison of Ablative Behaviour for ZrC and ZrC–Cu Doped Carbon/carbon Composites in Oxyacetylene Torch Environment

Ablation behaviour of Csf/ZrB2-SiC composites fabricated by direct ink writing and reactive melt infiltration

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Effect of preset interfacial ZrB 2 particles on the microstructure and properties of C/C-AlSi composites

Microstructure and Ablation Behavior of W Coating Prepared by Atmospheric Plasma Spraying for Zr/Cu Infiltrated C/C Composites

Microstructure and properties of C/C–ZrC composites with matrix modification by slurry infiltration

A novel optimized two-step method for preparing the Z-pin-like rods to improve their effect on the ablation resistance of C/C-ZrC-SiC

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Preparation and long-term ablation behavior of Cf-reinforced ZrC-SiC coated C/C-ZrC-SiC composite

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties