Oxidation And Ablation Resistance Of C-F/Zrc-Sic Ultra-High Temperature Composites
Guo Qian,Zhu Shizhen,Qiao Yanan,Liu Ling,Ma Zhuang
2015-01-01
Rare Metal Materials and Engineering
Abstract:ZrC has high melting point and high hardness, and SiC-ZrC composite has excellent oxidation resistance properties. Using the toughening mechanisms of carbon fiber, C-f/ZrC-SiC ultra-high temperature Composite has become a researching focus in high-temperature materials. In this paper, the ratio of ZrC: SiC in the matrix was 2:1, 4:1, 8:1 and 16:1. The composite materials with SiC coating were tested with plasma wind tunnel ablation under the condition of 2700 K and 600 s, in order to assess the microstructures and ablation behaviors of different composite materials. The composition and microstructure of the ablated samples were characterized by XRD, SEM and EDS, respectively. The results show that at the central area at 2700 K, SiC on the surface is rapidly oxidized, while oxidation and ablation begin to occur in the matrix. The higher the Zr content in the matrix is, the better oxidation and ablation resistance are. The ablation layer is thick, even up to a millimeter level. As the Si content increases, it produces more SiO2 which is easy to volatilize under the surface. The porosity in the ablation layer increases due to evaporation of SiO2, and then oxygen will be easier to go to the interior, which result in more severe erosion. Meanwhile, oxidized ZrO2 from ZrC in the matrix is fewer. The protection of carbon fiber decreases, and it is the reason why the ablation of the carbon fiber is more serious.