Abstract:We have previously reported the solvothermal synthesis of pure monoclinic and tetragonal zirconia nanoparticles in water and methanol. The solvent effect on this synthesis was studied further for this work. The effects of reaction temperature, reaction time and thermal treatment temperature on the crystal phases of the as-prepared hydrous ZrO2 precipitates formed from the solvothermal reaction of hydrated zirconyl nitrate (ZrO(NO3)2·2H2O) and urea were characterized by X-ray diffraction. Plausible mechanisms for the formation of hydrous precipitates, their transformation and their stabilization were examined. Precipitates formed initially with a tetragonal structure irrespective of the solvent used. These tetragonal precipitates, in water, transform into thermodynamically stable monoclinic structures as a result of higher precipitate solubility under hydrothermal conditions. Dissolution and precipitation processes are thus favored. The tetragonal structure was, however, maintained under methanothermal conditions probably due to poor precipitate solubility in methanol. The removal of water from precipitates by reaction with urea in methanol may make the tetragonal structure more rigid. This contributes to the maintenance of the tetragonal structure after precipitate thermal treatment (at 400 ℃). Differences in precipitate solubility and their reaction with urea in water and methanol may dictate the synthetic pathway for pure monoclinic and tetragonal ZrO2 via the solvothermal method.

Effects of Solvent on the Phase Composition and Microstructure of ZrSiO4 Film

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of Zirconia Powders by Sol-gel Process

Preparation of Zirconia/Organosilicone Thin Film by Sol-Gel Method

Solvent Effects on the Solvothermal Synthesis of PureMonoclinic and Tetragonal Zirconia Nanoparticles

Comparison of ZrO2-SiO2 Sols Synthesized by Two Methods: Preparation, Stability and Physical-Chemical Structure

Solvothermal synthesis of sub-micron spherical zirconia particles

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Effects of silica on phase transformation and microstructure of zirconia fiber

The Effects of Solvents on the Highly Oriented ZnO Films Prepared Using Sol–gel Method

The effects of solvents on the formation of Ba0.65Sr 0.35TiO3 thin films derived by sol-gel processing

Effect of crystal structure on optical properties of sol-gel derived zirconia thin films

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Preparation of Zirconia Thin Films Via Sol-Gel Process from Inorganic Precursor

ZrO<sub>2</sub> Thin Films Prepared by Self-Assembled Method

Annealing Effects on the Phase and Microstructure Transformations of Nanocrystalline (zro2)1−x(sc2o3)x (x=0.02–0.16) Thin Films Deposited by Sol–gel Method

The Study of the Silicon Dioxide Anti-Reflection Film Prepared by the Sol-Gel Method

The preparation of silica-based SiO2-ZrO2 films as waveguides by sol-gel process

Preparation of ZrC/SiC Porous Self-Supporting Monoliths Via Sol-Gel Process Using Polyethylene Glycol As Phase Separation Inducer

Infiltrating Between ZrO2 and SiO2 Sol-Gel Films

Solvents Effects on Structure and Morphology of SrMoO4 Films via Chemical Solution Processing