Abstract:Pure monoclinic (m) and tetragonal (t) zirconia nanoparticles were readily synthesized from the reaction of inorganic zirconium salts (e.g., hydrated zirconyl nitrate) and urea in water and methanol, respectively, via a facile solvothermal method. The role of the solvents was crucial in the formation of the pure ZrO2 phases, whereas their purity was essentially insensitive to other variables, including reaction temperature, reactant concentration, pH, and zirconium salts. Water as the solvent led to the transformation of hydrous ZrO2 precipitates initially formed with tetragonal structures to thermodynamically more stable m-ZrO2 via the dissolution-precipitation process, whereas methanol favored the removal of water molecules from the precursors via their reaction with urea, consequently maintaining the tetragonal structures. The obtained tetragonal samples were found to possess superior hydrothermal stability compared to those reported previously, which provides the possibility for systematically studying the effects of ZrO2 phases on many catalytic reactions involving water as a reactant or product. Using these pure m- and t-ZrO2 phases as supports, dispersed MoO, catalysts were synthesized at MoOx surface densities of similar to 5.0 Mo/nm(2), which is close to one monolayer of coverage. Characterization by X-ray diffraction and Raman spectroscopy confirmed that the pure ZrO2 phases remained unchanged in the presence of the MoOx domains and the MoO. domains existed preferentially as 2D polymolybdate structures. The catalysts were subsequently examined for selective methanol oxidation as a test reaction. m-ZrO2 support led to 2-fold greater oxidation rates than for t-ZrO2 support, reflecting the higher intrinsic reactivity of the MoO, domains on m-ZrO2. This is consistent with their higher reducibility probed by temperatureprogrammed reduction with H-2 (H-2 TPR). These observed effects of the ZrO2 phases provide the basis for designing catalysts with tunable redox properties and reactivity.

Solvent Effects on the Solvothermal Synthesis of PureMonoclinic and Tetragonal Zirconia Nanoparticles

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Effect of Reaction Temperature on Surface Morphology and Photoelectric Properties of ZnO Grown by Hydrothermal Method in Mixed Solvent

Effects of Precipitators and Surfactants on the Preparation of Zirconia Nanopowders via Solvothermal Method

Facile Synthesis Of Pure Monoclinic And Tetragonal Zirconia Nanoparticles And Their Phase Effects On The Behavior Of Supported Molybdena Catalysts For Methanol-Selective Oxidation

Preparation of Zirconia Powders by Sol-gel Process

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Influences of preparation parameters on the structural and catalytic performance of zirconia in isosynthesis

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Solvothermal Synthesis of Zirconia Nanomaterials: Latest Developments and Future

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Synthesis of Yttrium Oxide Nanocrystal Via Solvothermal Process

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Tetragonal‐to‐Monoclinic Phase Transitions in Nanocrystalline Rare‐Earth‐Stabilized Zirconia Prepared by a Mild Hydrothermal Method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Nanocrystalline Rare Earth Stabilized Zirconia: Solvothermal Synthesis Via Heterogeneous Nucleation-Growth Mechanism, and Electrical Properties

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Monoclinic zirconium oxide nanostructures synthesized by a hydrothermal route