Abstract:To improve the ablation and scouring resistance of C/C composites, powder with particle sizes of 0.5–1 μm, 1–3 μm and 10–20 μm were used as infiltration powder to prepare C/C-HfC-SiC composites, named HSV-0.5-1, HSV-1-3 and HSV-10-20, respectively. Results show that the agglomeration of the powder makes it difficult to form a uniform and dense ceramic layer on the sample surface. The content of HfC ceramics increases with the particle size of the initial powder. In addition, the grain size of HfC first increases and then becomes irregularly spherical as the initial powder particle size increases. After ablation for 40s, HSV-1-3 shows the best resistance to ablation due to the mixed crystal form of flakes and spheres that form a denser oxide film in the center of the ablation. In three subsequent room-temperature airflow scour tests, the oxide film of HSV-1-3 and HSV-10-20 were damaged in the sample surface. After following ablation for 40 s, HSV-10-20 showed good ablation resistance with the linear ablation of −0.75 μm/s. The reason is the high HfC content and dense ceramic layer contribute to the formation of a continuous and complete oxide layer that prevents oxygen diffusion during ablation. This work provides guidance on the use of particle size in the RMI.

Microstructure and Ablation Behavior of C/C–HfC Composites Prepared by Precursor Infiltration and Pyrolysis

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

Effect of HfC addition on ablation behavior of SiBCN ceramics

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Ablation behaviors and mechanisms of Cf/HfCPIP-SiCCVI composites: From SiO2 nanowires film to HfO2 skeleton

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Microstructure and ablation performance of HfC/PyC core-shell structure nanowire-reinforced Hf1-xZrxC coating

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Comparative ablation behaviors of C/SiC–ZrC and C/SiC–HfC composites prepared by ceramization of carbon aerogel preforms

UHTC coating reinforced by HfC nanowires against ablation for C/C composites