Abstract:Composites based on hafnium carbide and reinforced with continuous naked carbon fiber with and without PyC interface were prepared at low temperature by precursor infiltration and pyrolysis and chemical vapor deposition method. The microstructure, mechanical property, cyclic ablation and fiber bundle push-in tests of the composites were investigated. The results show that after three times ablation cycles, the bending strength of samples without PyC interface decreased by 63.6 %; the bending strength of samples with PyC interface only decreased by 37.8 %. The force displacement curve of the samples with PyC interface presented a well pseudoplastic deformation state. The mechanical behavior difference of two kinds of composites was due to crucial function of PyC interface phase including protection of fiber and weakening of fiber/matrix interface.

What problem does this paper attempt to address?

The paper primarily explores the cyclic ablation resistance and bending properties of 2D carbon fiber reinforced hafnium carbide composites (Cf/HfC composites) under two different interphase conditions (with and without PyC interphase). Specifically, the authors first prepared carbon fiber preforms containing a large amount of ceramic phase through the precursor infiltration and pyrolysis (PIP) method. They further densified these loose ceramic particles using the chemical vapor deposition (CVD) method, thereby obtaining high-density composites at relatively low temperatures. The study particularly focused on the role of the PyC interphase, which can form a protective layer on the fiber surface, reducing the bonding strength between the fibers and the matrix, thus favoring the improvement of the composite's toughness. Additionally, the study evaluated the cyclic ablation behavior of these two composites in a high-temperature oxygen environment and the changes in bending strength of the composites before and after ablation. Experimental results showed that after three ablation cycles, the bending strength of the samples without the PyC interphase decreased by approximately 63.6%, while the samples with the PyC interphase only decreased by 37.8%. This indicates that the PyC interphase can effectively protect the fiber structure from damage, reduce mass loss during the ablation process, and thus maintain a higher residual bending strength. Moreover, the composites containing the PyC interphase exhibited better pseudo-plastic deformation, which is beneficial for improving the toughness of the composites. In summary, this study aims to develop new carbon fiber reinforced hafnium carbide composites with excellent cyclic ablation resistance and good bending properties, and to improve the overall performance of the materials by introducing the PyC interphase.

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Effects of HfC/PyC Core-Shell Structure Nanowires on the Microstructure and Mechanical Properties of Hf1-xZrxC Coating

Flexural properties of cyclic ablated SiCf/HfC-SiC composites

Effect of PyC-SiC double-layer interface on ablation behaviour of impacted CVD-SiCnws/HfC coating

PyC interphase growth mechanism and control models of C/SiC composites

Microstructure and ablation performance of HfC/PyC core-shell structure nanowire-reinforced Hf1-xZrxC coating

Effect of pyrocarbon interphase texture and thickness on tensile damage and fracture in T‐700TM carbon fiber–reinforced silicon carbide minicomposites

Investigation on Cf/PyC Interfacial Properties of C/C Composites by the Molecular Dynamics Simulation Method

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Ablation behaviour and mechanical property of the B-modified SiC/HfC-SiC composites in cyclic ablation environment

Effect of PyC/BN interfacial phases on mechanical behavior of SiC/SiC composites

Effect of carbon matrix on mechanical and tribological properties of Cf/Cu/C composites

Influence of pyrolytic carbon interphase and pyrolysis temperature on the mechanical and tribological properties of Cf/SiC after heat treatment at 1800 °C

Damage Mechanism Analysis to the Carbon Fiber and Fiber-Ceramic Interface Tailoring of Cf/ZrC-SiC Using PyC Coating

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Effects of single-phase and Co-deposited interphases on mechanical hysteresis behavior in T700 TM mini-C f /SiC composites

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

The oxide-layer configuration alteration and pseudo-ductile crack propagation mechanisms in composites induced by different relative thicknesses of CVI HfC-SiC multiphase matrix

Effect of SiCnws on flexural strength of SiCf/HfC-SiC composites after impact and ablation

Mechanical Properties and Failure Behavior of 3D-SiCf/SiC Composites with Different Interphases