Abstract:The C/SiC-Cu3Si-Cu interpenetrating composites were prepared by the ceramization and metallization of carbon fiber reinforced carbon aerogel (C/CA) preforms. Fracture mechanical and ablation behaviors as well as their dependence on metal addition and PyC interface thickness were investigated. With the presence of metallic components, the C/SiC-Cu3Si-Cu composites show pseudo-plastic fracture, typical brittle-plastic mixed fracture, and then ladder-like fracture with the PyC interface thickness increasing due to the co-existence of ductile and brittle components, obviously different from the fracture of conventional ceramic matrix composites. The composite with 3.0 lm-thick interface has the highest flexural strength of 292.8 MPa due to the proper interfacial bond strength and residual compressive stress. The composite with 1.9 lm-thick interface has the highest work of fracture but relatively low fracture toughness due to the abundant modes of crack propagation. The anti-ablation property is deteriorated with increased PyC thickness due to the weakened transpiration cooling effect and reduced oxide scale quality. The composite with 0.9 lm-thick interface exhibits lower mass and linear ablation rates of 0.054 mg cm-2 s-1 and 0.018 lm s- 1 after ablation at 2200 degrees C for 600 s, respectively. This work provides vital insights into the control of the overall performance of carbon fiber reinforced ceramic-metal matrix composites.

Flexural properties of cyclic ablated SiCf/HfC-SiC composites

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Ablation behaviour and mechanical property of the B-modified SiC/HfC-SiC composites in cyclic ablation environment

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Effect of SiCnws on flexural strength of SiCf/HfC-SiC composites after impact and ablation

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Construction of sandwich-structured C/C-SiC and C/C-SiC-ZrC composites with good mechanical and anti-ablation properties

SiC Nanowires Toughed HfC Ablative Coating for C/C Composites

The mechanical properties of C/C-ZrC-SiC composites after laser ablation

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Preparation and Properties of C/SiC Composites Reinforced by High Thermal Conductivity Graphite Films

Ablation behaviors and mechanisms of Cf/HfCPIP-SiCCVI composites: From SiO2 nanowires film to HfO2 skeleton

Improvement of ablation resistance of CVD-HfC/SiC coating on hemisphere shaped C/C composites by introducing diffusion interface

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

Comparative ablation behaviors of C/SiC–ZrC and C/SiC–HfC composites prepared by ceramization of carbon aerogel preforms

Fracture Mechanical and Ablation Behaviors of C/SiC-Cu3Si-Cu Interpenetrating Composites and Their Dependence on Metal Addition and Interface Thickness

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation