Abstract:Due to the high modulus, high strength, low density, excellent wear resistance and good neutron absorption, the boron carbide (B4C) particle reinforced aluminum (Al) matrix composites have been widely applied in the aerospace, weaponry, transportation and neutron shielding fields. In response to the increasing requirement of better strength -ductility matching of B4C/Al composites, introducing a nano-scale reinforcement into the B4C/Al composites becomes an attractive research focus. In this work, the SiC nanowires were ball-milled with Al powders, and then the SiC/Al composite powders were mixed with B4C microparticles. Thus, the 15vol. % B4C/SiC/Al composites with different volume fractions of SiC nanowires were fabricated by hot-pressing sintering and hot extrusion. B4C microparticles and SiC nanowires are uniformly dispersed in the B4C/SiC/Al composites, while the introduced SiC nanowires effectively decrease the Al matrix grain sizes. B4C/SiC/Al composites produce the better strength-ductility matching than that of B4C/Al composites, while the 15vol. % B4C/SiC/Al composite with 1vol. % SiC nanowires achieved the best strength-ductility matching. It generates the 281.7 ± 2.7 MPa in yield strength, 351.2 ± 0.1 MPa in ultimate tensile strength and 5.9 ± 0.7% in failure elongation, which are increased by 18.2%, 15.1% and 13.5% compared to the B4C/Al composites. Uniformly dispersed B4C microparticles and SiC nanowires largely block the dislocation motions and improve the dislocation storage capacity, which results in a more significant hetero-deformation induced (HDI) hardening effect in the B4C/SiC/Al composites. Moreover, the B4C/Al interfacial transition regions with the added SiC nanowires becomes stronger, which can enhance the load transfer efficiency of the B4C/Al interfaces as a result of the existing dislocation hardening zones. In conclusion, it is a good strategy to combine the synergistic strengthening effect of micro-scale and nano-scale reinforcements in the metal matrix composites.

Ablation behaviour and mechanical property of the B-modified SiC/HfC-SiC composites in cyclic ablation environment

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Flexural properties of cyclic ablated SiCf/HfC-SiC composites

Effect of SiCnws on flexural strength of SiCf/HfC-SiC composites after impact and ablation

Effect of HfC addition on ablation behavior of SiBCN ceramics

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Preparation and Properties of C/SiC Composites Reinforced by High Thermal Conductivity Graphite Films

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

B4C-SiC skeleton reinforced graphite composites with excellent mechanical properties

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Improvement of ablation resistance of CVD-HfC/SiC coating on hemisphere shaped C/C composites by introducing diffusion interface

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Effect of SiCnws@BN core shell upon impact-ablation performance of HfC coating on C/C composites

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation behaviour of Csf/ZrB2-SiC composites fabricated by direct ink writing and reactive melt infiltration

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Ablation behaviors of ultra-high temperature ceramic composites

Ablation behaviors and mechanisms of Cf/HfCPIP-SiCCVI composites: From SiO2 nanowires film to HfO2 skeleton

Fabrication, microstructure characterization and mechanical properties of B4C microparticles and SiC nanowires hybrid reinforced aluminum matrix composites