Abstract:A tri-layer coating of mullite/Y2Si2O7/(70wt%Y2Si2O7+30wt%Y2SiO5) was prepared on carbon fiber reinforced silicon carbide (C/SiC) composite substrate through dip-coating route for the sake of improving oxidation resistance of C/SiC composites. An Al2O3–SiO2 sol with high solid content was selected as raw material for mullite, and a slurry of Y2O3 powder filled silicone resin was used to synthesize yttrium silicate. The microstructure, phase composition, and oxidation resistance of the coating were investigated. The as-fabricated coating shows high density and favorable bonding to C/SiC substrate. After oxidation at 1400 and 1500 °C for 30 min under static air, the flexural strengths of coated C/SiC composite were both increased by ~30%. The desirable thermal stability and the further densification are responsible for excellent oxidation resistance. With the additional help of compatible thermal expansion coefficients among substrate and sub-layers in coating, the coated composite retained 111.2% of original flexural strength after 12 times of thermal shock in air from 1400 °C to room temperature. The carbothermal reaction at 1600 °C between free carbon in C/SiC substrate and rich SiO2 in mullite resulted in severe frothing and desquamation of coating and obvious degradation in oxidation resistance.

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Cyclic ablation behaviors of mullite‐modified C/C–ZrC–SiC composites prepared by PIP

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Influence of precursor content on the microstructure and ablative resistance of CLVD-C/C-SiC-ZrC composites

Effect of HfC addition on ablation behavior of SiBCN ceramics

Ablation-resistant Ta0.78Hf0.22C solid solution ceramic modified C/C composites for oxidizing environments over 2200 °C

Ablation behaviors of ultra-high temperature ceramic composites

Preparation and Properties of C/SiC Composites Reinforced by High Thermal Conductivity Graphite Films

WSi2 modified HfB2-SiC coating: Microstructure and ablation resistance

Microstructure, Mechanical and Ablation Properties of Transpiration Cooling Applied to C/C-SiC Composite for Novel Anti-ablation Material

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C