Abstract:In order to improve the ablation and oxidation resistance of C/C–ZrC–SiC composites in wide temperature domain, "Z-pins like" Zr–Si–B–C multiphase ceramic rods are prepared in the matrix. The influence of different sintering temperatures on the microstructure of ceramic rods and the ablative behavior of heterogeneous composites are studied. The results showed that the ZrB2 and SiC phases are formed in the sintered matrix, and the increase of sintering temperature is beneficial to improve the density of the ceramic rods. The ablation properties of samples have been greatly improved. The mass and linear ablation rate are 0.8 mg/s and 3.85 μm/s, respectively, at an ablation temperature of 3000 °C and an ablation time of 60 s. After ablation, the matrix surface is covered with SiO2 and ZrO2 mixed oxide films. This is due to the preferential oxidation of "Z-pins like" Zr–Si–B–C multiphase ceramic rods in the ablation process, and B2O3 melt, SiO2 melt, borosilicate glass, ZrSiO4 melt and ZrO2 oxide film can be generated successively from the low-temperature segment to the ultra-high temperature segment. These oxidation products can be used as compensation oxide melts for the healing of cracks and holes on the matrix surface in different temperature ranges and effectively prevent the external heat from spreading into the matrix. Therefore, C/C–ZrC–SiC composites with "Z-pins like" Zr–Si–B–C multiphase ceramic rods achieve ablation resistance in wide temperature domain.

Cyclic ablation behaviors of mullite‐modified C/C–ZrC–SiC composites prepared by PIP

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Effect of mullite content on microstructure and ablation behavior of mullite modified C/C-SiC-HfC composites

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Laser ablation behavior and mechanism of Cf/SiC–ZrC ultra-high temperature ceramic matrix composite prepared by PIP method

Cyclic Ablation Properties of C/SiC-ZrC Composites

Ceramic Matrix Composite Cyclic Ablation Behavior under Oxyacetylene Torch

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Microstructure and ablation behaviour of C/C-SiC-ZrC-Cu composites prepared by reactive melt infiltration

Enhanced ablative resistance of C/C composites with densified ZrB 2 -based ceramics by incorporation of Mo as interface layer

Ablation behaviors of ultra-high temperature ceramic composites